- Polymer Property : CTE, linear = 6.61 µin/in-°F
Polymer Property : CTE, linear = 6.61 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.9 µm/m-°C @Temperature 0.000 - 100 °C |
6.61 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Kennametal Stellite Stellite® 12 PM with P/M Processing Applications: include vane plugs, fuel metering pins, spacer bushings, ball blanks (bearings), race blanks (bearings), diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wea.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 300 °C |
6.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
| International Mold Steel DH2F Pre-Hardened H13-Type Mold Steel Description: DH2F is one of the best machining pre-hardened H13-type steels available.Unique Characteristics: 38-42 HRc hardness.Through hardened for exceptional dimensional stability.Cuts mold maki.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 200 °C |
6.61 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 100 °C |
6.61 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Latrobe LSSâ„¢ 2367 Hot Work Tool Steel TLS 2367 is a chromium-molybdenum hot work steel that is similar to AISI H11 hot work steel, but which contains a higher molybdenum content. The higher molybdenum gives TLS 2367 better hot hardness .. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 0.000 - 100 °C |
6.61 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Kennametal Stellite Stellite® 12 Satisfactory finishing results can be obtained using carbide tipped tools. Applications include cutting plastics, rubber, paper, carpet, and wood; saw teeth, trimmer knives, carpet knives, ledger bl.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 242® alloy, cold rolled sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 204 °C |
6.61 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature <=538 °C |
6.61 µin/in-°F @Temperature <=1000 °F |
|
| AK Steel PH 15-7 Mo® Precipitation Hardening Stainless Steel, Condition TH 1050 AK Steel 15-7 Mo® provides high strength and hardness, good corrosion resistance and minimum distortion on heat treatment. It is easily formed in the annealed condition and develops effective bala.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 400 °C |
6.61 µin/in-°F @Temperature 68.0 - 752 °F |
|
| Assab Steels VANADIS 4 Cold Work Steel VANADIS 4 is a chromium-molybdenum-vanadium alloyed steel which is characterized by:High wear resistanceHigh compressive strengthVery good through-hardening propertiesVery good toughnessExcellent di.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 787 °C |
6.61 µin/in-°F @Temperature 68.0 - 1450 °F |
|
| ATI Allegheny Ludlum 430 Ferritic Stainless Steel Characteristics:oxidation resistant at elevated temperatures, corrosion resistance approaching nickel-bearing stainless steels in mildly corrosive environments, ductile, does not work harden readily.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 900 °C |
6.61 µin/in-°F @Temperature 68.0 - 1650 °F |
Type 441 |
| ATI Allegheny Ludlum Type AL 441HP™ Stainless Steel Alloy Allegheny Ludlum stainless Type AL 441HP™ alloy is a heat resisting ferritic grade providing good oxidation and corrosion resistance for applications like automotive exhaust system components. Dua.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 300 °C |
6.61 µin/in-°F @Temperature 572 °F |
|
| Bohler-Uddeholm BÖHLER S500(m42) High Speed Steel Description: Cobalt Molybdenum high speed steel processing high hardness, excellent cutting properties, high red hardness and good toughness. BOHLER S500 is also available in the special grade ISORA.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.61 µin/in-°F @Temperature 69.8 - 199 °F |
|
| Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1150 (Heated 621°C) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.61 µin/in-°F @Temperature 69.8 - 199 °F |
|
| Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1150M (Heated 760°C/2hr/AC then 621°C/4hr/AC) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 204 °C |
6.61 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 204 °C |
6.61 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 204 °C |
6.61 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 250 °C |
6.61 µin/in-°F @Temperature 68.0 - 482 °F |
|
| Schmolz + Bickenbach Cryodur® 2990 Cold Work Die Steel Description: Newly developed ledeburitic cold-work steel with high hardness, good toughness and high tempering resistance combined with high wear resistance.Applications: Cutting and punching tools .. |
|||