Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 8.00 µm/m-°C @Temperature 900 °C |
4.44 µin/in-°F @Temperature 1650 °F |
|
MarkeTech Repton 115 Aluminum Oxide Brand 115 features: High Density and Purity.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even whe.. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 900 °C |
4.44 µin/in-°F @Temperature 1650 °F |
|
MarkeTech Repton 125 Aluminum Oxide Brand 125 features: High Purity Standard.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even when t.. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 900 °C |
4.44 µin/in-°F @Temperature 1650 °F |
|
MarkeTech Repton 136 Aluminum Oxide Brand 136 features: Molding-structural.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even when the.. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 300 °C |
4.44 µin/in-°F @Temperature 572 °F |
|
MarkeTech Repton 835 Zirconia + 4 mol% Calcia Brand 835 features: High porosity.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even when thermal .. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 300 °C |
4.44 µin/in-°F @Temperature 572 °F |
|
MarkeTech Repton 837 Zirconia + 4.4 mol% Calcia Brand 837 features: Good spalling characteristics.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, ev.. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 900 °C |
4.44 µin/in-°F @Temperature 1650 °F |
|
MarkeTech Repton 837 Zirconia + 4.4 mol% Calcia Brand 837 features: Good spalling characteristics.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, ev.. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 300 °C |
4.44 µin/in-°F @Temperature 572 °F |
|
MarkeTech Repton 868 Zirconia + 8 mol% Yttria (YSZ) Brand 868 features: High density.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even when thermal c.. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 900 °C |
4.44 µin/in-°F @Temperature 1650 °F |
|
MarkeTech Repton EXP 338 Alumina 99.6% EXP 338 features high porosity.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even when thermal cyc.. |
|||
CTE, linear | 8.00 - 9.50 µm/m-°C @Temperature 25.0 - 100 °C |
4.44 - 5.28 µin/in-°F @Temperature 77.0 - 212 °F |
|
Materion E40 Beryllium/BeO Composite, 40 Volume% BeO Metal matrix composite made up principally of beryllium and crystal BeO platelets. Produced by blending the beryllium and beryllium oxide powders into a homogeneous mixture to create isotropic prop.. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 20.0 - 800 °C |
4.44 µin/in-°F @Temperature 68.0 - 1470 °F |
|
Misumi Alumina 96 Aluminum Oxide, Al2O3 Information provided by MISUMI Corporation. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 20.0 - 450 °C |
4.44 µin/in-°F @Temperature 68.0 - 842 °F |
|
H.C. Starck WCu 85/15 Tungsten-Copper Composite Material Description of Product: Tungsten-copper composite materials are produced by copper infiltration of porous sintered tungsten. They are available with different copper contents (10 - 30 %). A therm.. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature -30.0 - 70.0 °C |
4.44 µin/in-°F @Temperature -22.0 - 158 °F |
|
Schott F5 Glass Information Provided by SCHOTT North America, Inc. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature -30.0 - 70.0 °C |
4.44 µin/in-°F @Temperature -22.0 - 158 °F |
|
Schott N-BAK2 Glass Information Provided by SCHOTT North America, Inc. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature -30.0 - 70.0 °C |
4.44 µin/in-°F @Temperature -22.0 - 158 °F |
|
Schott N-SF15 Glass Information Provided by SCHOTT North America, Inc. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 20.0 - 300 °C |
4.44 µin/in-°F @Temperature 68.0 - 572 °F |
|
Schott N-SSK5 Glass Information Provided by SCHOTT North America, Inc. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 20.0 - 1000 °C |
4.44 µin/in-°F @Temperature 68.0 - 1830 °F |
|
CeramTec 665 Steatite, MgO•SiO2 Steatites used in place of aluminas are a cost-effective way to meet performance requirements. They are easier to form and fire at lower temperatures. 665 L533C has low dielectric loss. It makes exc.. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 20.0 - 1000 °C |
4.44 µin/in-°F @Temperature 68.0 - 1830 °F |
ASTM-C372 |
CeramTec Rubalit® 708 Alumina, 96% Based on 96% aluminum oxide, Rubalit® 708 was developed specifically for making heavy-duty resistors and miniature metal layer resistors. Because of its outstanding strength, this same material is .. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 20.0 - 1000 °C |
4.44 µin/in-°F @Temperature 68.0 - 1830 °F |
|
CeramTec Rubalit® 708S Alumina, 96% Rubalit® 708S (96%) is an alumina that features high strength and thermal conductivity. It provides outstanding results when used on commercially available thick-film pastes and metallization syste.. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 25.0 - 800 °C |
4.44 µin/in-°F @Temperature 77.0 - 1470 °F |
ASTM-C372 |
CoorsTek ADOS-90R 91% Alumina Thick Film Substrate This 91-percent alumina (nominal) formulation offers a dark brown body for special applications. Applications: thick films and lasers |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 25.0 - 800 °C |
4.44 µin/in-°F @Temperature 77.0 - 1470 °F |
ASTM-C372 |
CoorsTek ADS-995 99.5% Alumina Thin Film Applications: thin film substrates |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 25.0 - 1000 °C |
4.44 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM-C372 |
CoorsTek ADS-995R MidFilm™ 99.5% Alumina Thick Film Applications: thick films and lasers |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 25.0 - 800 °C |
4.44 µin/in-°F @Temperature 77.0 - 1470 °F |
ASTM-C372 |
CoorsTek ADS-996 99.6% Alumina Thin Film Applications: thin film substrates |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 30.0 - 400 °C |
4.44 µin/in-°F @Temperature 86.0 - 752 °F |
|
Ametek Molybdenum-Copper Composite AMC 7525 Information supplied by Ametek Specialty Metal Products.The material is available as finished parts with the following maximum dimensions:Width: 6 inches (152 mm)Thickness: 0.150 inches (3.8 mm)Leng.. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 20.0 - 1000 °C |
4.44 µin/in-°F @Temperature 68.0 - 1830 °F |
ASTM-C372 |
CeramTec CeramCool® Rubalit® 708 Alumina, 96% CeramCool® is a metallized ceramic heat-sink for high power applications demonstrated by high power LED-systems. CeramCool® material characteristics: electrical insulation, high volume resistivit.. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 20.0 - 1000 °C |
4.44 µin/in-°F @Temperature 68.0 - 1830 °F |
DIN 51045 |
CeramTec Rubalit® 708 HP Alumina, 96% (High Performance) Rubalit® 708 HP (High Performance) has been developed from Rubalit® 708S. This material shares the same chemical composition, is produced on the same plant and using the identical production techn.. |
|||
CTE, linear | 8.00 µm/m-°C @Temperature 100 °C |
4.44 µin/in-°F @Temperature 212 °F |
|
Chevron Phillips Ryton® R10 7006A PPS Polyphenylene Sulfide
(discontinued **) Ryton® PPS is used in many electronic and automotive applications because of its high strength, favorable electrical properties, and high temperature stability.Data provided by the manufacturer.Sol.. |