Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 48.0 µm/m-°C @Temperature 0.000 - 100 °C |
26.7 µin/in-°F @Temperature 32.0 - 212 °F |
Y-Direction; IPC-TM-650 2.4.41 |
Rogers Corporation RT/duroid® 5880 Glass Microfiber Reinforced PTFE High Frequency Laminate RT/duroid® 5870 and 5880 glass microfiber reinforced PTFE composites are designed for exacting stripline and microstrip circuit applications. Glass reinforcing microfibers are randomly oriented to.. |
|||
CTE, linear | 48.1 µm/m-°C @Temperature -40.0 °C |
26.7 µin/in-°F @Temperature -40.0 °F |
ASTM D696 |
Dow SPECTRIM™ HH 390 Reaction Moldable Polymer Information provided by Dow |
|||
CTE, linear | 48.0 µm/m-°C @Temperature -30.0 - 0.000 °C |
26.7 µin/in-°F @Temperature -22.0 - 32.0 °F |
100 x 15 x 3 mm sample; AZDEL Test |
Azdel Plus C300B04N 30% Chopped Fiber Mat / PP Resin Matrix AZDEL® C300B04N is a chopped fiber material based on random oriented long chopped glass fiber mat (paper making process). This polypropylene composite material features high flow properties and a .. |
|||
CTE, linear | 48.0 µm/m-°C @Temperature -30.0 - 0.000 °C |
26.7 µin/in-°F @Temperature -22.0 - 32.0 °F |
100 x 15 x 3 mm sample; AZDEL Test |
Azdel Plus C321B02N 32% Chopped Fiber Mat / PP Resin Matrix AZDEL® C321B02N is a chopped fiber material based on random oriented long chopped glass fiber mat (paper making process). This polypropylene composite material features high flow properties and a .. |