Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 15.7 - 16.7 µm/m-°C @Temperature 20.0 - 200 °C |
8.72 - 9.28 µin/in-°F @Temperature 68.0 - 392 °F |
|
PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 21.0 - 538 °C |
8.70 µin/in-°F @Temperature 69.8 - 1000 °F |
|
H.C. Starck MP35N® Nickel/Cobalt/Chromium/Molybdenum Alloy MP35N is a nickel-cobalt based alloy of the Multiphase® alloy system that has ultra high strength, toughness, ductility, biocompatibility, and outstanding corrosion resistance. H.C. Starck offers.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 230® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 700 °C |
8.72 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 700 °C |
8.72 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 700 °C |
8.72 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes HR-160® alloy, plate, aged 8000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 556® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 556® alloy, all-weld metal GTAW Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 20.0 - 982 °C |
8.72 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 21.0 - 538 °C |
8.72 µin/in-°F @Temperature 69.8 - 1000 °F |
|
Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 0% Cold Reduction Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 21.0 - 538 °C |
8.72 µin/in-°F @Temperature 69.8 - 1000 °F |
|
Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 45% Cold Reduction Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 21.0 - 538 °C |
8.72 µin/in-°F @Temperature 69.8 - 1000 °F |
|
Carpenter MP35N* Ni-Co-Cr-Mo Alloy, Cold Drawn 33%, Aged 565°C/4hr/AC Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 20.0 - 300 °C |
8.72 µin/in-°F @Temperature 68.0 - 572 °F |
|
ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 10% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 20.0 - 300 °C |
8.72 µin/in-°F @Temperature 68.0 - 572 °F |
|
ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 20% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 20.0 - 300 °C |
8.72 µin/in-°F @Temperature 68.0 - 572 °F |
|
ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 75% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 556® alloy, bar after 16000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |