Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 15.5 - 16.5 µm/m-°C @Temperature 20.0 - 200 °C |
8.61 - 9.17 µin/in-°F @Temperature 68.0 - 392 °F |
|
PEAK Werkstoff DISPAL S220 Aluminum Alloy, AlSi35, Condition O Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 0.000 - 900 °C |
8.61 µin/in-°F @Temperature 32.0 - 1650 °F |
|
Kennametal Stellite Stellite® 12 PM with P/M Processing Applications: include vane plugs, fuel metering pins, spacer bushings, ball blanks (bearings), race blanks (bearings), diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wea.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
Haynes Hastelloy® G-30® alloy, mill annealed HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 21.0 - 982 °C |
8.61 µin/in-°F @Temperature 69.8 - 1800 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 25.0 - 600 °C |
8.61 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes HR-160® alloy, annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 25.0 - 600 °C |
8.61 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 25.0 - 600 °C |
8.61 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 25.0 - 600 °C |
8.61 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 25.0 - 600 °C |
8.61 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 25.0 - 700 °C |
8.61 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
Haynes Hastelloy® G-30® alloy, 50% cold rolled and 5000 hours at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 25.0 - 600 °C |
8.61 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 21.1 - 649 °C |
8.60 µin/in-°F @Temperature 70.0 - 1200 °F |
|
Carlson C 600 Nickel-Chromium-Iron Alloy Carlson Alloy C 600 is nickel-chromium alloy, developed for use in severely corrosive environments at elevated temperatures. The high nickel content of this alloy provides excellent resistance to c.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 200 °C |
8.61 µin/in-°F @Temperature 68.0 - 392 °F |
|
ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 10% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 200 °C |
8.61 µin/in-°F @Temperature 68.0 - 392 °F |
|
ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 30% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 200 °C |
8.61 µin/in-°F @Temperature 68.0 - 392 °F |
|
ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 50% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
Haynes Hastelloy® G-30® alloy, 19.1 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |