- Polymer Property : CTE, linear = 15.4 µm/m-°C
Polymer Property : CTE, linear = 15.4 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.4 µm/m-°C @Temperature 20.0 - 900 °C |
8.56 µin/in-°F @Temperature 68.0 - 1650 °F |
|
| Kennametal Stellite Deloro® 40G Nickel base. Good combination of wear resistance, corrosion resistance, machinability, and repairability. Machined with tungsten carbide tools, using slow speeds and light feeds. Finish grinding ach.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, all-weld metal GTAW Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, cold rolled, solution annealed sheet, 0.8-2.8 mm thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 20.0 - 250 °C |
8.56 µin/in-°F @Temperature 68.0 - 482 °F |
|
| ATI Allegheny Ludlum AL 20™ Sheet and Strip Specialty Steel The N08020 alloy has been available for many years and has found applications in many environments, such as in chlorides and in sulfuric and sulfurous acids.Although AL 20 alloy was developed for im.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||