- Polymer Property : CTE, linear = 14.9 µm/m-°C
Polymer Property : CTE, linear = 14.9 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.9 µm/m-°C @Temperature 0.000 - 900 °C |
8.28 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6K 1.6 mm thick sheet 13.3 mm^3 volume loss--abrasive wear data. Applications include agitators, augers, ball mills, banbury mills, cams, crusher bearings, dryers, dry presses, dump cars, fans, filters, food machinery, g.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 20.0 - 871 °C |
8.28 µin/in-°F @Temperature 68.0 - 1600 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 20.0 - 871 °C |
8.28 µin/in-°F @Temperature 68.0 - 1600 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 20.0 - 871 °C |
8.28 µin/in-°F @Temperature 68.0 - 1600 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 20.0 - 871 °C |
8.28 µin/in-°F @Temperature 68.0 - 1600 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 20.0 - 871 °C |
8.28 µin/in-°F @Temperature 68.0 - 1600 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 20.0 - 871 °C |
8.28 µin/in-°F @Temperature 68.0 - 1600 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 540 °C |
8.28 µin/in-°F @Temperature 77.0 - 1000 °F |
|
| Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, hot rolled, solution annealed plate, 6.4-12.7 mm (1/2 in.) thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 30.0 - 427 °C |
8.28 µin/in-°F @Temperature 86.0 - 801 °F |
|
| Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet, GTAW weld HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 30.0 - 427 °C |
8.28 µin/in-°F @Temperature 86.0 - 801 °F |
|
| Haynes Hastelloy® G-30® alloy, 50% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 30.0 - 427 °C |
8.28 µin/in-°F @Temperature 86.0 - 801 °F |
|
| Haynes Hastelloy® G-30® alloy, 50% cold rolled and 5000 hours at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 30.0 - 427 °C |
8.28 µin/in-°F @Temperature 86.0 - 801 °F |
|
| Haynes Hastelloy® G-30® alloy, 6.4 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 30.0 - 427 °C |
8.28 µin/in-°F @Temperature 86.0 - 801 °F |
|
| Haynes Hastelloy® G-30® alloy, 9.5 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 21.0 - 700 °C |
8.28 µin/in-°F @Temperature 69.8 - 1290 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 50% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of .. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 24.0 - 871 °C |
8.28 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 24.0 - 871 °C |
8.28 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 24.0 - 871 °C |
8.28 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 20.0 - 871 °C |
8.28 µin/in-°F @Temperature 68.0 - 1600 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 649 °C |
8.28 µin/in-°F @Temperature 1200 °F |
|
| Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy UDIMET® alloy L-605 (UNS R30605) is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°.. |
|||