- Polymer Property : CTE, linear = 14.4 µm/m-°C
Polymer Property : CTE, linear = 14.4 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 500 °C |
8.00 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Osprey Metals CE11 Al-Si Controlled Expansion Alloy Al-50%Si controlled expansion alloy manufactured and patented by Osprey Metals Ltd.Information provided to MatWeb by Osprey Metals. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 600 °C |
8.00 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 600 °C |
8.00 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 600 °C |
8.00 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 600 °C |
8.00 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 425 °C |
8.00 µin/in-°F @Temperature 77.0 - 797 °F |
|
| Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 425 °C |
8.00 µin/in-°F @Temperature 77.0 - 797 °F |
|
| Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 30.0 - 316 °C |
8.00 µin/in-°F @Temperature 86.0 - 601 °F |
|
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GMAW spray weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 30.0 - 316 °C |
8.00 µin/in-°F @Temperature 86.0 - 601 °F |
|
| Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet, GTAW weld HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 30.0 - 316 °C |
8.00 µin/in-°F @Temperature 86.0 - 601 °F |
|
| Haynes Hastelloy® G-30® alloy, 30% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 30.0 - 316 °C |
8.00 µin/in-°F @Temperature 86.0 - 601 °F |
|
| Haynes Hastelloy® G-30® alloy, 50% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 30.0 - 316 °C |
8.00 µin/in-°F @Temperature 86.0 - 601 °F |
|
| Haynes Hastelloy® G-30® alloy, 50% cold rolled and 5000 hours at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 30.0 - 316 °C |
8.00 µin/in-°F @Temperature 86.0 - 601 °F |
|
| Haynes Hastelloy® G-30® alloy, plate and bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 21.0 - 538 °C |
8.00 µin/in-°F @Temperature 69.8 - 1000 °F |
Mean |
| Special Metals INCONEL® 718SPF™ Nickel Superalloy, Annealed + Aged Typical annealing - continuous process anneal, 1700°F (927°C) at 15 ft (4.57 m) per minute. This produces ASTM No. 12 grain size. Typical aging - 1750°F (954°C)/1 h/AC plus 1325°F (.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 21.0 - 93.0 °C |
8.00 µin/in-°F @Temperature 69.8 - 199 °F |
|
| AK Steel PH 15-7 Mo® Precipitation Hardening Stainless Steel, Condition A AK Steel 15-7 Mo® provides high strength and hardness, good corrosion resistance and minimum distortion on heat treatment. It is easily formed in the annealed condition and develops effective bala.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 27.0 - 316 °C |
8.00 µin/in-°F @Temperature 80.6 - 601 °F |
|
| ATI Allegheny Ludlum AL 200™ Nickel Alloy, UNS N02200 Ferromagnetic. Allegheny Ludlum AL 200 alloy is wrought commercially pure nickel. This alloy provides highly ductile mechanical properties across a wide temperature range. Either alloy provides c.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 538 °C |
8.00 µin/in-°F @Temperature 68.0 - 1000 °F |
|
| ATI Allegheny Ludlum Altemp® 718 Nickel-Base Superalloy, Solution Treated Plate, UNS N07718 Allegheny Ludlum Altemp 718 alloy is an austenitic nickel-base superalloy which is used in applications requiring high strength to approximately 760 degrees Celsius and oxidation resistance to appro.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 1000 °C |
8.00 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| ATI Allegheny Ludlum Ohmaloy® 30 Resistance Alloy Ohmaloy 30 alloy is a moderately magnetic, ductile stainless steel having extremely high electrical resistivity. In addition to imparting high electrical resistivity, the aluminum content in these .. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 600 °C |
8.00 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 600 °C |
8.00 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 600 °C |
8.00 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 30.0 - 316 °C |
8.00 µin/in-°F @Temperature 86.0 - 601 °F |
|
| Haynes Hastelloy® G-30® alloy, 31.8 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 1000 °C |
8.00 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| ATI Allegheny Ludlum ALFA-I™ Stainless Steel Type 406 Characteristics:superior oxidation resistance for the temperature range 1600°F-over 2200°F, high electrical resistivity, high resistance to sulfidation, high resistance to carburization. Applicat.. |
|||