Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy sheet Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 0% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 40% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 40% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 50% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature sheet after 100 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 500 °C |
7.56 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 263® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 500 °C |
7.56 µin/in-°F @Temperature 69.8 - 932 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 900 °C |
7.56 µin/in-°F @Temperature 69.8 - 1650 °F |
Mean |
Dura-Bar 100-70-03 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 20.0 - 1000 °C |
7.56 µin/in-°F @Temperature 68.0 - 1830 °F |
|
ATI Allegheny Ludlum AL 468™ Dual Stabilized- Low Titanium Stainless Steel Characteristics:good corrosion resistance in a wide range of environments, can be used in annealed cold formed or as-welded conditions. Applications: used in place of Type 304 in an oxidizing when .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 20.0 - 1000 °C |
7.56 µin/in-°F @Temperature 68.0 - 1830 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™ (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 20.0 - 1000 °C |
7.56 µin/in-°F @Temperature 68.0 - 1830 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 70% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 500 °C |
7.56 µin/in-°F @Temperature 69.8 - 932 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Sheet, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 500 °C |
7.56 µin/in-°F @Temperature 69.8 - 932 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |