Thermal Properties | Metric | English | Comments |
---|---|---|---|
Specific Heat Capacity | 0.653 J/g-°C @Temperature 700 °C |
0.156 BTU/lb-°F @Temperature 1290 °F |
|
Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Specific Heat Capacity | 0.653 J/g-°C @Temperature 700 °C |
0.156 BTU/lb-°F @Temperature 1290 °F |
|
Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Specific Heat Capacity | 0.653 J/g-°C @Temperature 700 °C |
0.156 BTU/lb-°F @Temperature 1290 °F |
|
Haynes HR-160® alloy, annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Specific Heat Capacity | 0.653 J/g-°C @Temperature 700 °C |
0.156 BTU/lb-°F @Temperature 1290 °F |
|
Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Specific Heat Capacity | 0.653 J/g-°C @Temperature 700 °C |
0.156 BTU/lb-°F @Temperature 1290 °F |
|
Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Specific Heat Capacity | 0.653 J/g-°C @Temperature 700 °C |
0.156 BTU/lb-°F @Temperature 1290 °F |
|
Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Specific Heat Capacity | 0.653 J/g-°C @Temperature 700 °C |
0.156 BTU/lb-°F @Temperature 1290 °F |
|
Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Specific Heat Capacity | 0.653 J/g-°C @Temperature 700 °C |
0.156 BTU/lb-°F @Temperature 1290 °F |
|
Haynes HR-160® alloy, plate, aged 8000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Specific Heat Capacity | 0.653 J/g-°C @Temperature 700 °C |
0.156 BTU/lb-°F @Temperature 1290 °F |
|
Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Specific Heat Capacity | 0.653 J/g-°C @Temperature 700 °C |
0.156 BTU/lb-°F @Temperature 1290 °F |
|
Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Specific Heat Capacity | 0.653 J/g-°C @Temperature 700 °C |
0.156 BTU/lb-°F @Temperature 1290 °F |
|
Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |