Thermal Properties | Metric | English | Comments |
---|---|---|---|
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.455 J/g-°C | 0.109 BTU/lb-°F | |
Special Metals INCONEL® alloy 783 Ni-Co-Fe Alloy The newest of the high-performance superalloys invented by Special Metals Corporation, INCONEL® alloy 783 (UNS R30783/US Patent 5,478,417), is an oxidation-resistant, low expansion, nickel-cobalt.. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |