- Polymer Property : Specific Heat Capacity = 0.435 J/g-°C
Polymer Property : Specific Heat Capacity = 0.435 J/g-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 200 °C |
0.104 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 200 °C |
0.104 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 230® alloy, 0% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 200 °C |
0.104 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 200 °C |
0.104 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 200 °C |
0.104 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 230® alloy, 30% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 200 °C |
0.104 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 200 °C |
0.104 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 200 °C |
0.104 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature >=100 °C |
0.104 BTU/lb-°F @Temperature >=212 °F |
|
| Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature >=100 °C |
0.104 BTU/lb-°F @Temperature >=212 °F |
|
| Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature >=100 °C |
0.104 BTU/lb-°F @Temperature >=212 °F |
|
| Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature >=100 °C |
0.104 BTU/lb-°F @Temperature >=212 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature >=100 °C |
0.104 BTU/lb-°F @Temperature >=212 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature >=100 °C |
0.104 BTU/lb-°F @Temperature >=212 °F |
|
| Haynes Multimet® alloy, GTAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature >=100 °C |
0.104 BTU/lb-°F @Temperature >=212 °F |
|
| Haynes Multimet® alloy, investment-cast, as-cast Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C | 0.104 BTU/lb-°F | |
| HP Alloys Alloy 718, 0% Cold Worked, Not Aged 0% Cold Worked, Not Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes .. |
|||
| Specific Heat Capacity | 0.435 J/g-°C | 0.104 BTU/lb-°F | |
| HP Alloys Alloy 718, 25% Cold Worked, Aged 25% Cold Worked, Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Int.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C | 0.104 BTU/lb-°F | |
| HP Alloys Alloy 718, 50% Cold Worked 50% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 20.0 - 100 °C |
0.104 BTU/lb-°F @Temperature 68.0 - 212 °F |
|
| Special Metals DURANICKEL® 301 (UNS N03301) Annealed Rod and Bar Tensile strength (ultimate and yield), compressive strength, hardness, and elongation values reported here are typical for Annealed Rod and Bar specifically. Other property values are typical of ann.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 20.0 - 100 °C |
0.104 BTU/lb-°F @Temperature 68.0 - 212 °F |
|
| Special Metals DURANICKEL® 301 (UNS N03301) Annealed Wire Tensile strength (ultimate) and elongation values reported here are typical for Annealed Wire specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the alloy in gen.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 20.0 - 100 °C |
0.104 BTU/lb-°F @Temperature 68.0 - 212 °F |
|
| Special Metals DURANICKEL® 301 (UNS N03301) Hot-Finished Rod and Bar Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Hot-Finished Rod and Bar specifically. Other property values are typical of annealed DURANICKELÂ.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 20.0 - 100 °C |
0.104 BTU/lb-°F @Temperature 68.0 - 212 °F |
|
| Special Metals DURANICKEL® 301 (UNS N03301) Spring Wire Tensile strength (ultimate) and elongation values reported here are typical for Spring Wire specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the alloy in gener.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C | 0.104 BTU/lb-°F | |
| Special Metals INCONEL® 718SPF™ Nickel Superalloy, Annealed Typical annealing - continuous process anneal, 1700°F (927°C) at 15 ft (4.57 m) per minute. This produces ASTM No. 12 grain size. Heat capacity, melting range, moduli, and Poisson's ratio re.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C | 0.104 BTU/lb-°F | |
| Special Metals INCONEL® 718SPF™ Nickel Superalloy, Annealed + Aged Typical annealing - continuous process anneal, 1700°F (927°C) at 15 ft (4.57 m) per minute. This produces ASTM No. 12 grain size. Typical aging - 1750°F (954°C)/1 h/AC plus 1325°F (.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature >=100 °C |
0.104 BTU/lb-°F @Temperature >=212 °F |
|
| Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature >=100 °C |
0.104 BTU/lb-°F @Temperature >=212 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 25% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C | 0.104 BTU/lb-°F | |
| HP Alloys Alloy 718, 10% Cold Worked, Aged 10% Cold Worked, Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Int.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 200 °C |
0.104 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 200 °C |
0.104 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 200 °C |
0.104 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||