Thermal Properties | Metric | English | Comments |
---|---|---|---|
Melting Point | 549 - 664 °C | 1020 - 1230 °F | |
PEAK Werkstoff DISPAL S690 Aluminum Alloy, AlCu4MgAg, Condition T4 High stiffness and elongation at rupture. Property data for Condition T4 (Quench in water at RT).Information provided by PEAK Werkstoff GmbH |
|||
Melting Point | 549 - 664 °C | 1020 - 1230 °F | |
PEAK Werkstoff DISPAL S690 Aluminum Alloy, AlCu4MgAg, Condition T6 High stiffness and elongation at rupture. Property data for Condition T6 (Quench in water at RT).Information provided by PEAK Werkstoff GmbH |
|||
Melting Point | 548 - 660 °C | 1020 - 1220 °F | |
Materion AMC225XE T4 Aluminum/Silicon Carbide MMC Extruded Bar Aluminium alloy 2124 reinforced with 25 volume % silicon carbide particles (average size 3 micron). It is manufactured by a powder metallurgy route using high-energy mixing to ensure excellent part.. |
|||
Melting Point | 548 - 660 °C | 1020 - 1220 °F | |
Materion AMC225XE T4 Aluminum/Silicon Carbide MMC Forged Plate Aluminium alloy 2124 reinforced with 25 volume % silicon carbide particles (average size 3 micron). It is manufactured by a powder metallurgy route using high-energy mixing to ensure excellent part.. |
|||
Melting Point | 549 °C | 1020 °F | |
Heatbath/Park 10699 Class IV Salt Neutral Salt Basically the same as Uni-Hard, except that it is formulated per MIL-S-10699-B, Class 4Information provided by Heatbath Corporation - Park Metallurgical. |
|||
Melting Point | 549 °C | 1020 °F | |
Heatbath/Park Uni-Hard IR High Speed Hardening Salt Frequently used as a preheat for tool hardening or as a heating medium for continuous production hardening. Dragout is minimal because of high fluidity. Uni-Hard IR is water-soluble and non-hygros.. |
|||
Melting Point | 549 °C | 1020 °F | |
Heatbath/Park Uni-Hard IR Neutral Salt Frequently used as a preheat for tool hardening or as a heating medium for continuous production hardening. Dragout is minimal because of high fluidity. Uni-Hard IR is water-soluble and non-hygros.. |
|||
Melting Point | 549 °C | 1020 °F | |
Heatbath/Park Uni-Hard IR Quenching and Tempering Salt Frequently used as a preheat for tool hardening or as a heating medium for continuous production hardening. Dragout is minimal because of high fluidity. Uni-Hard IR is water-soluble and non-hygros.. |
|||
Melting Point | 549 °C | 1020 °F | |
Heatbath/Park Uni-Hard IR Steel Brazing Neutral Salt Used for brazing similarly to Nu-Sal. It is more stable than Nu-Sal in the higher temperature range.Information provided by Heatbath Corporation - Park Metallurgical. |
|||
Melting Point | 550 - 580 °C | 1020 - 1080 °F | |
Solvay Chemicals Potassium Fluoroaluminate Potassium fluoroaluminate (KalF4) is used for the production of welding agents, production of soldering agents, and for the production of abrasives Potassium fluoroaluminate: CAS-No.: 60304-36-1 (SD.. |
|||
Melting Point | >= 548 °C | >= 1020 °F | Solidus |
CRP Technology AMC225xe Aluminum Alloy - SiC Composite, T4 Condition AMC225xe is a high quality aerospace grade aluminum alloy (AA2124) reinforced with 25% by volume of ultrafine particles of silicon carbide. It is manufactured by a special powder metallurgy route us.. |