Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 19.2 µm/m-°C @Temperature 20.0 °C |
10.7 µin/in-°F @Temperature 68.0 °F |
ASTM data |
Dow Questra® WA207 High Heat Syndiotactic Polystyrene, 30% Glass Filled
(discontinued **) QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve.. |
|||
CTE, linear, Parallel to Flow | 19.2 µm/m-°C @Temperature 20.0 °C |
10.7 µin/in-°F @Temperature 68.0 °F |
ASTM data |
Dow Questra® WA552 High Heat Syndiotactic Polystyrene, 30% Glass Filled
(discontinued **) QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve.. |
|||
CTE, linear, Parallel to Flow | 19.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
10.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
SABIC Innovative Plastics LNP THERMOCOMP PX01658 PA 6 LNP* Thermocomp* PX01658 is a compound based on Nylon 6 containing Proprietary Fillers. |