Polymer Property : Flexural Modulus = 187 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	1.29 GPa	187 ksi	2% Secant, Injection Molded Sample, 0.05 in/min test speed; ASTM D790
Ineos N00N-00 Polypropylene Impact Copolymer Grade N00N-00 is a fractional melt flow rate, high impact copolymer polypropylene specifically designed for non-pressure structured wall pipe but can also be used in other extrusion applications req..
Flexural Modulus	1.29 GPa	187 ksi	1% secant; ASTM D790-02
Ipiranga Petrochem PCC 2314 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr..
Flexural Modulus	1.29 GPa	187 ksi	at 1% secant modulus; ASTM D790
A. Schulman POLYAXIS® PD2000 Polypropylene DescriptionPolyaxis PD 2000 is a polypropylene specifically designed from rotational molding.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and E..
Flexural Modulus	1.29 GPa	187 ksi	at 1% secant modulus; ASTM D790
A. Schulman POLYAXIS® PD2000 Polypropylene DescriptionPolyaxis PD 2000 is a polypropylene specifically designed from rotational molding.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and E..
Flexural Modulus	1.29 GPa	187 ksi	at 1% secant modulus; ASTM D790
A. Schulman POLYAXIS® PD2000 Polypropylene DescriptionPolyaxis PD 2000 is a polypropylene specifically designed from rotational molding.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and E..
Flexural Modulus	1.29 GPa	187 ksi	at 1% secant modulus; ASTM D790
A. Schulman POLYAXIS® PD2000 Polypropylene DescriptionPolyaxis PD 2000 is a polypropylene specifically designed from rotational molding.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and E..
Flexural Modulus	1.29 GPa	187 ksi	at 1% secant modulus; ASTM D790
A. Schulman POLYAXIS® PD2000 Polypropylene DescriptionPolyaxis PD 2000 is a polypropylene specifically designed from rotational molding.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and E..
Flexural Modulus	1.29 GPa	187 ksi	ISO 178
Cathay PA514 Renewable Engineering Polyamide Cathay engineering polyamides contain 26-100% renewably sourced material. Advantages: Operates at similar conditions to PA66; Suitable for injection, compounding and extrusion; Stable mechanical pr..
Flexural Modulus	1.29 GPa	187 ksi	ASTM D-790
Bapolene® 3257U Polyethylene, Injection Molding Bapolene 3257U is a high density polyethylene resin that offers improved cycle times, superior modulus and impact resistance. It complies with US FDA 21CFR177.1520 and has a UV protection package.A..
Flexural Modulus	1.29 GPa	187 ksi	at 1% secant modulus; ASTM D790
A. Schulman POLYAXIS® PD2000 Polypropylene DescriptionPolyaxis PD 2000 is a polypropylene specifically designed from rotational molding.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and E..