Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
Nylene® Norpex® AX235 PPE (Polyphenylene Ether) Properties for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
Flexural Modulus | 2.30 GPa @Temperature 23.0 °C |
334 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYabs P0P ABS, Plating Grade Information provided by Polykemi AB |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® CX5640 PC+ABS Cycoloy* CX5640 is a all purpose PC+ABS blend specially developed for applications requiring weld line strength. High heat resistance combined with good flow, excellent impact and low temperature du.. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® LG9000 PC+ABS PC+ABS blend, low gloss and UV-stable, suitable for automotive interior applications. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® XCY620 PC+ABS PC+ ABS Automotive applications, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® 4401R PPC+PC (Asia Pacific) LEXAN 4401R is a high heat resistant poly(ester)carbonate injection molding resin.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® 4701R PC (Europe-Africa-Middle East) LEXAN 4701R is a copolymer of polyphthalate carbonate resin for applications requiring high heat resistance. This grade has higher heat properties compared to Lexan 4501. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® 943A PC (Europe-Africa-Middle East) LEXAN 943A is a medium viscosity flame retardant, UV-stabilized grade. UL-94 V0 listed and available in transparent and tints. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® 9945A PC (Europe-Africa-Middle East) Lexan* resin 9945A Polycarbonate (PC)is a non-filled, injection moldable grade. This non-chlorinated, non-brominated PC has an UL-94 V0 rating at 1.8 mm. Lexan resin 9945A is available in clear tr.. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® EXL9132 PC Copolymer Opaque PC-Siloxane copolymer with excellent processability. Improved flow, low temperature ductility, UV stabilized. Non-chlorinated, non-brominated flame retardant product. UL rated V0/5VA. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® FXD141R PC (Europe-Africa-Middle East) LEXAN FXD141R is a transparent/translucent medium viscosity grade for light diffusion effects. Internal mold release. The color package may affect performance. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® HPS1S PC High flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, e-beam and gamma sterilizable. Contains.. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® LSHF PC (Europe-Africa-Middle East) Clear PolyCarbonate, High Flow, UV Stabilization, Heat Stabilization |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® PC1000 PC (Asia Pacific) PC1000 resin is a medium-low flow (MFR = 10 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold rele.. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® PC2200 PC (Europe-Africa-Middle East) PC2200 resin is a high flow (MFR = 22 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® PK2870 PC (Europe-Africa-Middle East) LEXAN* PK2870 polycarbonate resin, global grade, MVR (300C/1.2kg) 2 cm3/10min, high viscosity, branched, blow molding, high melt strength, high impact resistance, Available in transparent colors onl.. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® VR2820 PC (Europe-Africa-Middle East) VR 2820 resin is a low flow (MFR = 7 at 300ºC/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the extrusion market. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 80x10x4 mm specimen, 2 mm/min; ISO 178 |
Solvay Engineered Polymers SEQUEL® 1820 Engineered Polyolefin
(discontinued **) Description: SEQUEL® 1820 engineered polyolefin is designed for automotive exterior applications that require energy management combined with excellent ductility and stiffness over a broad temperat.. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Geloy XTPM302 ASA+PC (Europe-Africa-Middle East) XTPM302 is a general purpose ASA/PC injection moulding grade, available in various colors.Typical properties measured on natural material.This data was supplied by SABIC-IP for the Europe-Africa-Mid.. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® 144R PC UL rated HB. 200 series recommended when V-2 rating required. MFR 10.5. Internal mold release. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade will no longer .. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
Gichem GILAC D160/MT Acrylonitrile Butadiene Styrene
(discontinued **) ABS with good resilience, good thermal properties. Medium-High Injection speed.Information provided by GICHEM Gruppo Industriale Chimico |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min; ASTM D790 |
Lavergne VYTEEN PC 135 General Purpose Medium Viscosity Polycarbonate Vyteen PC 135, Black, medium viscosity polycarbonate, has an excellent balance of stiffness and impact resistanceFeatures: - High heat resistance - Good processabilityInformation provided by Biegl.. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics PC0800 PC (Europe-Africa-Middle East) PC0800 resin is a low flow (MFR = 8 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics PC2200R PC (Europe-Africa-Middle East) PC2200R resin is a high flow (MFR = 22 at 300ºC/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.This data was supplied by S.. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | 23°C, 50% RH; ASTM D790 |
Asahi Kasei Xyron® 100V Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
Ascend Performance Materials Vydyne® R220 Nylon 66, 40% mineral reinforced, Conditioned Vydyne® R220 is a 40% mineral-reinforced PA66 resin formulated for improved impact strength. Available in natural, it is an injection-molding grade formulated to retain the inherent processing adva.. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
Ashley Polymers Ashlene® 829L Nylon 6 Basic Nylon 6, low viscosity, lubricated.Data provided by the manufacturer |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
BASF Ultramid® B3L BK00464 PA6 (Dry) Description: Impact-modified, free-flowing and rapidly processable injection-molding grade for dry impact-resistant technical articles such as, for example, housings, fittings, small parts and wall .. |
|||
Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
Total Lacqrene® 2901 Medium Impact Polystyrene
(discontinued **) LACQRENE® 2901 is a very easy flowing, medium impact polystyrene for injection molding. The very high flow of this grade allows for the production of thin wall section or long flow path molding on.. |