Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.24 GPa | 180 ksi | Tangent; ASTM D790 |
RheTech Products FRp256-01 Polypropylene Copolymer, Flame Retardant, Black Applications: Electrical component housingsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | Tangent; ASTM D790 |
RheTech Products FT4500-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Automotive componentsDurable goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | Tangent; ASTM D790 |
RheTech Products FT4802-01UV Thermoplastic Polyolefin, UV Stabilized, Black Applications: Bodyside moldings and claddingsFacia and bumper coversInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
Network Polymers NPP 50-0753 Description: High Density Polyethylene (HDPE)Information provided by Network Polymers Inc. |
|||
Flexural Modulus | 1.24 - 2.76 GPa | 180 - 400 ksi | Average value: 1.99 GPa Grade Count:18 |
Overview of materials for PETG Copolyester This property data is a summary of similar materials in the MatWeb database for the category "PETG Copolyester". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790 |
Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 10% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and .. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790 |
Honeywell Aegis™ PL56HS High Viscosity, Heat Stabilized, Flexible Nylon 6/66 Copolymer
(discontinued **) Description: Aegis PL56HS is a high viscosity, heat stabilized, flexible nylon 6/66 copolymer. It possesses a balance of flexibility, toughness and abrasion resistance. Combined with its high melt v.. |
|||
Flexural Modulus | 1.24 GPa @Temperature 23.0 °C |
180 ksi @Temperature 73.4 °F |
ASTM D790A |
Ineos H36G-00 Polypropylene Homopolymer This is a high flow rate homopolymer. This material is designed for fiber spinning and spun bonded processes. It meets the requirements of the U.S. Food and Drug Administration as specified in 21 .. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790 |
Multibase Multi-Flex® D 6500 TPO Thermoplastic Polyolefin Elastomer Features: Chemical Resistance, Good PaintableOzone Resistant General PurposeDensity, LowTear Strength, GoodUV Resistance, Good Forms:PelletsProcessing Method:Blow Molding Uses: Automotive Applica.. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | tangent; ASTM D790 |
Spartech PP7220 Calcium Carbonate Filled High Impact Copolymer Provides the highest level of impact of all copolymers and are useful in applications where improved processing and stiffness are required versus unfilled copolymer materials.Information provided by.. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790 |
Sterigenics Raprex® R-200 Branched High Density Polyethylene Applications: Injection Molding and ExtrusionRAPREX® R-200 is a high density polyethylene based resin that exhibits an excellent balance of melt processability and physical properties due to its .. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | 5 mm/min, tangent; ASTM D790 |
A. Schulman PP 1621 Polypropylene Low Flow Homopolymer Polypropylene DescriptionPolypropylene PP 1621 is a low flow homopolymer polypropylene primarily used for sheet strapping and profile extrusion applications.ApplicationPP 1621 meets FDA Regulation 21 CFR 177.1520.. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790 |
A. Schulman PP 828S-01 Polypropylene Medium Impact Molding Grade Polypropylene DescriptionPolypropylene PP 828S-01 is a medium impact molding grade created for applications needing good impact and higher H.D.T., such as tote bins, automotive ducting and housings. Information p.. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | 1.3mm per min, 1% secant; ASTM D790 |
Formosa Plastics Formolene® 6507N Impact Copolymer Polypropylene Impact Copolymer for Injection Molding Formolene® 6507N is a medium impact copolymer of polypropylene characterized by its easy mold flow, physical property balance and excellent dimensional stabil.. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | 5 mm/min, tangent; ASTM D790 |
A. Schulman PP 1621 Polypropylene Low Flow Homopolymer Polypropylene DescriptionPolypropylene PP 1621 is a low flow homopolymer polypropylene primarily used for sheet strapping and profile extrusion applications.ApplicationPP 1621 meets FDA Regulation 21 CFR 177.1520.. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790 |
A. Schulman POLYTROPE™ TPP 518 Injection Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 518 is an injection grade olefinic thermoplastic elastomer. This mineral filled product is recommended for applications requiring high stiffness and low thermal expansion i.. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | 5 mm/min, tangent; ASTM D790 |
A. Schulman PP 1621 Polypropylene Low Flow Homopolymer Polypropylene DescriptionPolypropylene PP 1621 is a low flow homopolymer polypropylene primarily used for sheet strapping and profile extrusion applications.ApplicationPP 1621 meets FDA Regulation 21 CFR 177.1520.. |
|||
Flexural Modulus | 1.24 GPa @Temperature 22.8 °C |
180 ksi @Temperature 73.0 °F |
ASTM D790 |
Ensinger TECAFINE™ PP Polypropylene (PP) TECAFINE™ PP is an anti-stated, polypropylene, random copolymer polyolefin engineering plastic providing excellent chemical resistance and high purity. FDA compliant with better mechanical propert.. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790A |
Dow 5D49 Polypropylene Homopolymer Resin OverviewConsistent processabilitySuperior spinning characteristicsComplies with U.S. FDA 21 CFR 177.1520 (c)1.1aDOW 5D49 Polypropylene Resin is intended for use in fiber spinning processes. It is w.. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | Secant @ 1% strain; ASTM D790 |
Bapolene® PP5082 Polypropylene, Injection Grade Bapolene PP 5082 is a multipurpose, high flow impact copolymer with excellent color and processability. This resin also exhibits a superior balance of stiffness and impact strength. This product m.. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790 |
Americas Styrenics EC6600 High Impact Polystyrene Product CharacteristicsExcellent printabilityMatte surface finishHigh heat distortion temperatureGood low temperature toughnessFood Contact CompliantTypical ApplicationsLithographic sheetPrinted toy.. |
|||
Flexural Modulus | 1.24 - 13.1 GPa | 180 - 1900 ksi | Average value: 2.86 GPa Grade Count:96 |
Overview of materials for Acetal Copolymer, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, PTFE Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790 |
A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer DescriptionPolypropylene PP 3052X-01 is an extra high flow impact resistant copolymer with relatively high stiffness. Information provided by A. Schulman. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790 |
A. Schulman POLYTROPE™ TPP 518 Injection Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 518 is an injection grade olefinic thermoplastic elastomer. This mineral filled product is recommended for applications requiring high stiffness and low thermal expansion i.. |
|||
Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790-92 |
Lubrizol Stat-Rite® SIS535 Static Control System Product Description: Stat-Rite® SIS535 is a static dissipative HIPS alloy. Stat-Rite SIS535 utilizes the patented Stat-Rite inherently dissipative polymer (IDP) alloy system to provide clean, perma.. |
|||
Flexural Modulus | 1.24 - 1.52 GPa | 180 - 220 ksi | ASTM D790 |
Buckeye Polymers BP RPPC 1720 TURXF Polypropylene, Talc Filled Product Information: Our Talc filled product lines exhibit excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and .. |