Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 10% Plasticizer (discontinued **)

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Propionate, Molded
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 10% Plasticizer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and ContainersProcessing: Injection Molding (Melt Temperature: 460°F, Mold Temperature: 150°F)Data supplied by Albis Plastics Corporation.

Physical Properties	Metric	English	Comments
Density	1.21 g/cc	0.0437 lb/in³	ASTM D792
Water Absorption	1.6 %	1.6 %	(24 hr); ASTM D570
Linear Mold Shrinkage	0.0020 - 0.0060 cm/cm	0.0020 - 0.0060 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	39.3 MPa	5700 psi	ASTM D638
Tensile Strength, Yield	31.7 MPa	4600 psi	ASTM D638
Flexural Yield Strength	41.4 MPa	6000 psi	ASTM D790
Flexural Modulus	1.24 GPa	180 ksi	ASTM D790
Izod Impact, Notched	2.46 J/cm	4.61 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	78.0 °C	172 °F	ASTM D648
Vicat Softening Point	102 °C	216 °F	ASTM D1525

Processing Properties	Metric	English	Comments
Melt Temperature	238 °C	460 °F	Injection
Mold Temperature	66.0 °C	151 °F