Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.320 GPa | 46.4 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Nima™ HL 18400 HDPE High Density Polyethylene - Halogenated FR compound with good impact resistance. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepa.. |
|||
Flexural Modulus | 0.320 GPa | 46.4 ksi | ASTM D790 |
ExxonMobil Iotek® 8000 Sodium Ionomer Molding/Extrusion Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A sodium ionomer with excellent abrasion resistance, impact strength, hardness and tensile strength. IOTEK ionomers provide superb low temperature .. |
|||
Flexural Modulus | 0.320 GPa | 46.4 ksi | ASTM D790 |
Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK) AvaSpire® AV-630 is an unreinforced polyaryletherketone (PAEK) developed as an alternative to low melt flow PEEK for the extrusion of ultra-thin films. Films with thicknesses as low as 0.2 mils (.. |
|||
Flexural Modulus | 0.320 GPa | 46.4 ksi | At 2 mm/min; ISO 178 |
Borealis Bormed™ LE6607-PH LDPE for Pharmaceutical Blow Molding Bormed LE6607-PH is a LD-polyethylene produced in a high pressure process intended for blow molding of sot and flexible packages for pharmaceutical products.Bormed LE6607-PH can be used in "blow-fil.. |
|||
Flexural Modulus | 0.320 - 0.520 GPa | 46.4 - 75.4 ksi | ASTM D790 |
Zeus THV Tubing THV Tubing is a Terpolymer of Tetrafluoroethylene, Hexafluoropropylene and Vinylidene fluoride. THV is the most flexible fluoropolymer available and has the highest degree of optical clarity. |
|||
Flexural Modulus | 0.320 GPa | 46.4 ksi | ISO 178 |
Chengdu Polyster FH7560 Thermoplastic Polyether-ester Elastomer (TPEE) Blend of H7560 and self-made flame retardant material. Flame retardant, high tear resistance. Applications requiring flame retardancy, such as wires, cables and optical fiber.Information provided by.. |
|||
Flexural Modulus | 0.320 GPa | 46.4 ksi | ASTM D790 |
Covestro Bayflex® 110-50 CM Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and o.. |
|||
Flexural Modulus | 0.320 GPa @Temperature 65.0 °C |
46.4 ksi @Temperature 149 °F |
ASTM Test |
BASF Ultramid® 8281 HS PA6 (Dry) |
|||
Flexural Modulus | 0.320 GPa | 46.4 ksi | ASTM D790 |
Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK)
(Unverified Data**) AvaSpire AV-630 is an unreinforced polyaryletherketone (PAEK) developed as an alternative to low melt flow PEEK for the extrusion of ultra-thin films. Films with thicknesses as low as 0.2 mils (5 mi.. |
|||
Flexural Modulus | 0.320 GPa | 46.4 ksi | ASTM D790 |
Suzhou Hipro Polymers Hiprolon® 211 ESNNHL P40 Nylon Hiprolon® 211ESNNHL P40 is a long chain polyamide compound from bio-renewable resource. It features low density, low water absorption, high dimension stability, high cold impact resistance, high bu.. |