Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 24.8 GPa @Temperature 87.8 °C |
3600 ksi @Temperature 190 °F |
Wet (2hr water boil immersion); ASTM D790 |
Park Electrochemical Nelcote® E-722 Epoxy Prepreg, 285 Kevlar® Reinforced Nelcote® E-722 is a modified 350°F cure epoxy system with excellent processing characteristics for vacuum bag, press, and autoclave molding.Key Features and Benefits:Epoxy resin system optimized f.. |
|||
Flexural Modulus | 24.8 GPa @Temperature 71.1 °C |
3600 ksi @Temperature 160 °F |
Dry; ASTM D790 |
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 285 Kevlar® Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle.. |
|||
Flexural Modulus | 24.8 GPa @Temperature -53.9 °C |
3600 ksi @Temperature -65.0 °F |
Dry; ASTM D790 |
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 285 Kevlar® Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle.. |
|||
Flexural Modulus | 24.8 GPa @Temperature 23.9 °C |
3600 ksi @Temperature 75.0 °F |
Dry; 325°F Autoclave Cured; ASTM D790 |
Park Electrochemical Nelcote® F-502 Phenolic Prepreg, 7781 E-Glass Reinforced Nelcote® F-502 is a MIL-R-9299 phenolic resin system suitable for impregnation on any MIL-C-9084 fabric with a compatible finish. F-502 is used in the manufacture of ablative reinforcements in rock.. |
|||
Flexural Modulus | 24.8 GPa @Temperature 23.9 °C |
3600 ksi @Temperature 75.0 °F |
0° Direction, Dry; ASTM D790 |
Park Electrochemical Nelcote® V-376 Cyanate Ester Epoxy Prepregs, 581 Quartz Reinforced Nelcote® V-376 is a Cyanate Ester matrix providing excellent electrical and mechanical properties for harsh aircraft, shipboard, and undersea applications for Radomes, Antenna, and Reflectors. Simp.. |
|||
Flexural Modulus | 24.8 GPa @Temperature 82.2 °C |
3600 ksi @Temperature 180 °F |
0° Direction, Wet; ASTM D790 |
Park Electrochemical Nelcote® V-376 Cyanate Ester Epoxy Prepregs, 581 Quartz Reinforced Nelcote® V-376 is a Cyanate Ester matrix providing excellent electrical and mechanical properties for harsh aircraft, shipboard, and undersea applications for Radomes, Antenna, and Reflectors. Simp.. |
|||
Flexural Modulus | 24.8 GPa @Temperature 177 °C |
3600 ksi @Temperature 351 °F |
Wet condition - 96 hours in boiling H2O |
Hexcel® HexPly® F650 Bismaleimide Resin with Fiberglass 7781 fabric reinforcement Laminate Physicals: 53% Fiber volume, 29% Resin content, 0.5% VoidsInformation provided by HexCel |