Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 40.0 MPa @Temperature 700 °C, Time 3.60e+7 sec |
5800 psi @Temperature 1290 °F, Time 10000 hour |
|
Outokumpu 4841 High Temperature Austenitic Stainless Steel Variant of 1.4845 with an increased silicon content which enhances the steel's resistance to oxidation/corrosion but has also made it more susceptible to embrittlement.Applications: Heat and creep r.. |
|||
Rupture Strength | 40.0 MPa @Temperature 700 °C, Time 3.60e+7 sec |
5800 psi @Temperature 1290 °F, Time 10000 hour |
|
Outokumpu 4845 High Temperature Austenitic Stainless Steel Standardized high-temperature steel for use at temperatures up to 1100°C in dry air. Prone to embrittlement after exposure between 600-900°C. Applications: Heat and creep resistance. For use o.. |
|||
Rupture Strength | 40.0 MPa @Temperature 815 °C, Time 36000 sec |
5800 psi @Temperature 1500 °F, Time 10.0 hour |
Typical Stress-Rupture |
Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C) Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200°F (650°C). It is principally used in low stress elevated temperature applications requiring reas.. |
|||
Rupture Strength | 40.0 MPa @Temperature 850 °C, Time 3.60e+7 sec |
5800 psi @Temperature 1560 °F, Time 10000 hour |
Stress Rupture |
AFE Technologies Cronite 34Ni/25Cr/Nb No. HR 33 Nb High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AF.. |