Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 386 MPa @Temperature 704 °C, Time 3.60e+6 sec |
56000 psi @Temperature 1300 °F, Time 1000 hour |
|
Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Rupture Strength | 386 MPa @Temperature 760 °C, Time 360000 sec |
56000 psi @Temperature 1400 °F, Time 100 hour |
|
Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Rupture Strength | 386 MPa @Temperature 760 °C, Time 360000 sec |
56000 psi @Temperature 1400 °F, Time 100 hour |
|
Haynes 282® Nickel Alloy Sheet, Gamma-Prime Strengthened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b.. |
|||
Rupture Strength | 386 MPa @Temperature 704 °C, Time 3.60e+6 sec |
56000 psi @Temperature 1300 °F, Time 1000 hour |
|
Haynes 282® Nickel Alloy Sheet, Gamma-Prime Strengthened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b.. |
|||
Rupture Strength | 386 MPa @Temperature 750 °C, Time 266000 sec |
56000 psi @Temperature 1380 °F, Time 74.0 hour |
forged; 4.4% elong |
Special Metals NIMONIC® alloy 91 Ni-Cr-Co Alloy NIMONIC® alloy 91 is a wrought nickel-chromium-cobalt based alloy strengthened by additions of aluminum and titanium.This alloy is a modification of NIMONIC alloy 90, but has an increased chromium .. |