Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 15.0 MPa @Temperature 900 °C, Time 3.60e+7 sec |
2180 psi @Temperature 1650 °F, Time 10000 hour |
|
Outokumpu 353MA® High Temperature Austenitic Stainless Steel Alloy with higher nickel content than the other steels. Has increased silicon and nitrogen contents and is microalloyed with rare earth metals (REM). Max service temperature in air is 1150°C, but.. |
|||
Rupture Strength | 15.0 MPa @Temperature 800 °C, Time 3.60e+7 sec |
2180 psi @Temperature 1470 °F, Time 10000 hour |
|
Outokumpu 4878 High Temperature Austenitic Stainless Steel Heat-resistant variant of 1.4541, with a slightly higher max carbon content. Recommended max service temperature for this steel in dry air is 800°C. Applications: Heat and creep resistance. For .. |
|||
Rupture Strength | 15.0 MPa @Temperature 815 °C, Time 3.60e+6 sec |
2180 psi @Temperature 1500 °F, Time 1000 hour |
Typical Stress-Rupture |
Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C) Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200°F (650°C). It is principally used in low stress elevated temperature applications requiring reas.. |
|||
Rupture Strength | 15.0 MPa @Temperature 1038 °C, Time 3.60e+6 sec |
2180 psi @Temperature 1900 °F, Time 1000 hour |
Sheet |
Special Metals UDIMET® alloy 188 Cobalt-base Alloy UDIMET® alloy 188 (UNS R30188) is a cobalt-base alloy with excellent high-temperature strength and good oxidation resistance to 2000°F (1093°C). The high chromium level coupled with small .. |
|||
Rupture Strength | 15.0 MPa @Temperature 950 °C, Time 3.60e+7 sec |
2180 psi @Temperature 1740 °F, Time 10000 hour |
Stress Rupture |
AFE Technologies Cronite 657 Nickel Alloy Castings High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AF.. |