Polymer Property : Tensile Strength, Ultimate = 164000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	1130 - 1380 MPa	164000 - 200000 psi
Materion Beryllium Copper Alloy 165 Plate & Rolled Bar; HT (TH04) Temper; over 25 to 51 mm Thickness (UNS C17000) Treatment required for max strength: 2 hrs @ 330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In..
Tensile Strength, Ultimate	1130 - 1380 MPa	164000 - 200000 psi
Materion Beryllium Copper Alloy 165 Rod and Bar; HT (TH04) Temper; over 25.4 to 76 mm (UNS C17000) Treatment required for max strength: 2-3 hrs @ 315-330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materi..
Tensile Strength, Ultimate	1130 - 1320 MPa	164000 - 191000 psi
Materion Beryllium Copper Alloy 25 Forgings & Extrusions; AT (TF00) Temper (UNS C17200) Treatment required for max strength: 3 hrs @ 330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In..
Tensile Strength, Ultimate	1130 - 1380 MPa	164000 - 200000 psi
Materion Beryllium Copper Alloy 25 Plate & Rolled Bar; AT (TF00) Temper; All Thicknesses (UNS C17200) Treatment required for max strength: 3 hrs @ 330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In..
Tensile Strength, Ultimate	1130 - 1380 MPa	164000 - 200000 psi
Materion Beryllium Copper Alloy 25 Rod and Bar; AT (TF00) Temper; over 76 mm (UNS C17200) Treatment required for max strength: 3 hrs @ 315-330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Material..
Tensile Strength, Ultimate	1130 - 1350 MPa	164000 - 196000 psi
Materion Beryllium Copper Alloy 25 Strip; AT (TF00) Temper (UNS C17200) Treatment required for max strength: 3 hrs @ 315ÂºCStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 96%Stress Relaxation after 1000 hrs @ 200Â°C: 70%Superficial Hardness: 30N 56-6..
Tensile Strength, Ultimate	1130 - 1380 MPa	164000 - 200000 psi
Materion Beryllium Copper Alloy 25 Tube; AT (TF00) Temper; over 76 mm o.d. (UNS C17200) Treatment required for max strength: 3 hrs @ 315-330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Material..
Tensile Strength, Ultimate	1130 - 1380 MPa	164000 - 200000 psi
Materion Beryllium Copper Alloy M25 Rod and Bar; AT (TF00) Temper; up to 76 mm (UNS C17300) Treatment required for max strength: 3 hrs @ 315-330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Material..
Tensile Strength, Ultimate	1130 MPa	164000 psi
Industeel SuperplastÂ® 350 Mold Steel SUPERPLASTÂ® 350 offers improved machinability, improved consistency and weldability, improved thermal conductivity, with a higher hardness allowing better mechanical properties and polishability...
Tensile Strength, Ultimate	1130 MPa	164000 psi
Haynes 230Â® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Ultimate	1130 - 1380 MPa	164000 - 200000 psi
Materion Beryllium Copper Alloy 25 Rod and Bar; AT (TF00) Temper; up to 76 mm (UNS C17200) Treatment required for max strength: 3 hrs @ 315-330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Material..
Tensile Strength, Ultimate	1130 - 1380 MPa	164000 - 200000 psi
Materion Beryllium Copper Alloy 25 Tube; AT (TF00) Temper; up to 76 mm o.d. (UNS C17200) Treatment required for max strength: 3 hrs @ 315-330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Material..
Tensile Strength, Ultimate	1130 - 1380 MPa	164000 - 200000 psi
Materion Beryllium Copper Alloy M25 Rod and Bar; AT (TF00) Temper; over 76 mm (UNS C17300) Treatment required for max strength: 3 hrs @ 315-330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Material..
Tensile Strength, Ultimate	1130 MPa	164000 psi
Haynes 625 alloy, plate after 4000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Ultimate	1130 MPa	164000 psi
Haynes 625 alloy, plate after 8000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Ultimate	1130 MPa @Temperature 540 Â°C	164000 psi @Temperature 1000 Â°F
Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650Â°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i..
Tensile Strength, Ultimate	1130 MPa @Thickness 50.8 mm, Temperature 21.1 Â°C	164000 psi @Thickness 2.00 in, Temperature 70.0 Â°F
Latrobe LescalloyÂ® 6305 VAC-ARC ; High Strength Alloy Steel LESCALLOY 6305 VAC-ARC steel is a modified 4140 steel with higher molybdenum and a vanadium addition. The alloy steel is generally used in the 160/180,000 psi tensile strength range obtained with a..
Tensile Strength, Ultimate	1130 MPa	164000 psi
TIMET TIMETAL® 6-2-4-6 Titanium Alloy (Ti-6Al-2Sn-4Zr-6Mo), 50% Equiaxed Alpha + Annealed This entry has UTS, TYS, Elongation, ROA, and fatigue values specific to material in the 50% Equiaxed Alpha + Annealed (705°C/1hr/AC) condition. Other data below are typical of TIMETAL® 6-2-4-6. ..
Tensile Strength, Ultimate	1130 MPa	164000 psi
Elgiloy® Co-Cr-Ni Alloy, Strip, 20% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati..
Tensile Strength, Ultimate	1131 MPa	164000 psi
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1075 (Heated 579°C) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio..
Tensile Strength, Ultimate	1130 MPa	164000 psi
Carpenter Gall-Tough PLUS™ Stainless, Annealed, 30% Cold Work Data provided by Carpenter Technology Corporation.Annealed 1150°C, water quenched, and cold drawn.Threshold Galling Stress 48 MPa. The avg. total volume loss on the wear test is 10.6 mm³ at 100 r..