Polymer Property : Tensile Strength, Ultimate = 13300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	92.0 MPa	13300 psi	ASTM Data
Dow Questra® QA804 High Heat Syndiotactic Polystyrene, 30% Glass Filled (discontinued **) QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Tensile Strength, Ultimate	92.0 MPa	13300 psi	ASTM Data
Dow Questra® WA202 High Heat Syndiotactic Polystyrene, 30% Glass Filled (discontinued **) QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Tensile Strength, Ultimate	92.0 MPa @Temperature 1150 Â°C	13300 psi @Temperature 2100 Â°F
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Tensile Strength, Ultimate	92.0 MPa	13300 psi	ASTM D638
Plenco 6500 Phenolic, Briquette, Transfer Molded PLENCO 06500 is a glass reinforced phenolic molding compound offering improved strength, dimensional stability, and excellent electrical properties. UL recognized under component file E40654. 06500 ..
Tensile Strength, Ultimate	92.0 MPa @Temperature 160 °C	13300 psi @Temperature 320 °F	ISO 527-1/-2
DSM Stanyl® TW271B3 (PA46+PTFE)-CF15 15% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified
Tensile Strength, Ultimate	92.0 MPa	13300 psi	ASTM D638
A. Schulman ComAlloy Hiloy® 114 Polypropylene, Glass Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.40% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	92.0 MPa	13300 psi	ASTM D638
A. Schulman ComAlloy Aqualoy® 143 Polypropylene, Glass Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.40% Glass Reinforced. In Aqualoy® materials, carefully selected base resins and proprietary additives meld hydrolytic stability an..
Tensile Strength, Ultimate	92.0 MPa	13300 psi	ISO value at 5mm/min.
BASF Capron® 8331G HI HS BK-102 Impact Modified, 14% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron 8331G HI HS BK-102 is a black pigmented, heat stabilized, 30% glass reinforced, impact modified polyamide 6 injection molding compound developed for applications requiring improved dry as mol..
Tensile Strength, Ultimate	92.0 MPa	13300 psi	ISO value at 5mm/min.
BASF Capron® GR20 20% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron GR20 is a 20% glass reinforced polyamide 6 injection molding compound possessing a balance of engineering properties combined with excellent processability and surface aesthetics. It is also..
Tensile Strength, Ultimate	92.0 MPa	13300 psi	ISO value at 5mm/min.
BASF Capron® GR20 HS 20% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron GR20 HS is a heat stabilized 20% glass reinforced polyamide 6 injection molding compound possessing a balance of engineering properties combined with excellent processability and surface aest..