Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 30.0 - 215 MPa | 4350 - 31200 psi | Average value: 149 MPa Grade Count:581 |
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Tensile Strength, Ultimate | 25.0 - 215 MPa @Strain 1.00 - 10.0 % |
3630 - 31200 psi @Strain 1.00 - 10.0 % |
Average value: 88.6 MPa Grade Count:5 |
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Tensile Strength, Ultimate | 25.0 - 215 MPa @Temperature -40.0 - 150 °C |
3630 - 31200 psi @Temperature -40.0 - 302 °F |
Average value: 88.6 MPa Grade Count:5 |
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Tensile Strength, Ultimate | 25.0 - 215 MPa @Temperature -55.0 - 275 °C |
3630 - 31200 psi @Temperature -67.0 - 527 °F |
Average value: 109 MPa Grade Count:18 |
Overview of materials for Polyetheretherketone, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Glass Fiber Filled". Each property range of values reported is minimum and maximum.. |