Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 7318 GREY The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | ASTM D412 |
Multibase Multi-Flex® TPE D 4201 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | ASTM D412 |
Multibase Multi-Flex® TPE G 7455 BLK Flame retardant thermoplastic rubber based on Shell's Kraton G polymers, manufactured under Shell's license. Product exhibits VO rating. Multi-Flex TPE contains Kraton™ G.Data provided by Multiba.. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 5003 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 8.30 MPa @Temperature 49.0 °C |
1200 psi @Temperature 120 °F |
Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 460 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 8.30 MPa @Temperature 49.0 °C |
1200 psi @Temperature 120 °F |
Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 660 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | ASTM D638/D412 |
Covestro Baydur® 646 Polyurethane Structural Foam RIM, Density 25 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | |
Dow DOWLEX™ 2503.10 Linear Low Density Polyethylene, Narrow MW Distribution DOWLEX® 2503.10 Polyethylene resin is a narrow molecular weight distribution copolymer designed as a superior processing resin. For very thin wall higher cavitation molding, this grade often is a p.. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | |
Dow LDPE 959I Low Density Polyethylene DOW LDPE 959I resin is a medium molecular weight distribution homo polymer designed to offer excellent clarity and flexibility with low warpage for lids. This resin has good processability over a wi.. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
Dow Nordel® IP 4640 Dense Extruded Profile FormulationNordel® IP 4640 |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | ASTM D638 |
Buckeye Polymers BP Flex A9008 TPO TPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment. These resins have excellent UV resistance and have a.. |