Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 7.79 MPa | 1130 psi | post cured- 2 hours at 177°C |
Multibase SILASTIC® C7-4565 VAROX Dow-Corning Biomedical Grade ETR Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 7.79 MPa | 1130 psi | post cured- 8 hours at 177°C; ASTM D412 |
Multibase C6-350 LH Parts A and B Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 7.79 MPa | 1130 psi | |
Dow Corning HV 1540/20P BASE AND CLEAR CURING AGENT 32 Shore, very low viscosity, castable hydrophobic silicone rubber with high tear strength and low temperature cure.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 7.79 MPa | 1130 psi | |
Dow Corning SILASTIC® Q7-4780 BIOMEDICAL GRADE ETR ELASTOMER, KIT Two-part, platinum-catalyzed (1:1 by weight), enhanced tear-resistant silicone elastomers are heat cured high consistency silicone rubbers designed for use by customers fabricating medical devices.I.. |