Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | >= 450 MPa | >= 65300 psi | |
Kobe Steel KS70 Commercially Pure Titanium, ASTM Gr. 3, Annealed Nominal Composition: Ti-Fe-OApplications: Tube sheets.Features: Relatively high strength, excellent corrosion resistance.Information provided by Kobe Steel |
|||
Tensile Strength, Ultimate | >= 450 MPa | >= 65300 psi | |
MetalTek C86500 Low Tensile Manganese Bronze High aqueous and atmospheric corrosion resistance, moderate strength and conductivity.Applications: Valves, pumps, pipe fittings, electric terminal ends.Information provided by MetalTekCast UNS C836.. |
|||
Tensile Strength, Ultimate | >= 450 MPa | >= 65300 psi | |
MetalTek HAYNES® HR120 Severe Corrosion and Heat Resistant Alloy Information provided by MetalTek |
|||
Tensile Strength, Ultimate | >= 450 MPa | >= 65300 psi | |
MetalTek MTEK E Cast UNS N24130 Nickel-Copper Alloy Acid and alkaline resistant. Weldable gradeApplications: Marine pumps, valves, seal housings, filter parts.Information provided by MetalTek |
|||
Tensile Strength, Ultimate | 450 MPa @Temperature 870 °C |
65300 psi @Temperature 1600 °F |
|
Haynes 188 alloy, hot rolled and 1175°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Tensile Strength, Ultimate | >= 450 MPa | >= 65300 psi | |
MetalTek MTEK 25-35Nb Heat Resistant Stainless Steel Information provided by MetalTekCast ASTM A297 MOD. |
|||
Tensile Strength, Ultimate | >= 450 MPa | >= 65300 psi | |
MetalTek MTEK 28-48WCo Heat Resistant Stainless Steel Information provided by MetalTek |
|||
Tensile Strength, Ultimate | >= 450 MPa | >= 65300 psi | |
MetalTek MTEK 30-20 Cast UNS N08604 Heat Resistant Stainless Steel Provides strength levels of HK with improved corrosion resistance to hot gases.Applications: Similar to HN.Information provided by MetalTekCast UNS N08604; Cast Grade HL; Cast ASTM A297, A608 |
|||
Tensile Strength, Ultimate | 450 MPa | 65300 psi | |
Sapco S.SiC Silicon Carbide Information provided by Sapco. |
|||
Tensile Strength, Ultimate | 450 - 550 MPa | 65300 - 79800 psi | |
CLAL-MSX ARCAP Anticorrosion AP1 H12 1/2 hard, Rolled Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
Tensile Strength, Ultimate | 450 MPa | 65300 psi | As Cast |
AFE Technologies Cronite 657 Nickel Alloy Castings High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AF.. |
|||
Tensile Strength, Ultimate | >= 450 MPa | >= 65300 psi | |
AK Steel ASTM A 607 Class 2 Formable, Grade 55K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy (HSLA) ASTM A 607 is for Hot Rolled and Cold Rolled grades. AK Steel produces Type 1 (columbium bearing only), Class 2 limits only C and has a 10 ksi difference between the minimum specified YS and UTS. .. |
|||
Tensile Strength, Ultimate | >= 450 MPa | >= 65300 psi | |
AK Steel ZINCGRIP® FORMABLE 50K / ASTM A1008 class 1 / SAE J1392 050 XLK, Grade 50 Electrogalvanized Carbon Steel, High Strength Low Alloy Steel (HSLAS) Information provided by AK Steel |
|||
Tensile Strength, Ultimate | 450 MPa | 65300 psi | |
Ametek P430L P/M Stainless Steel, Sintered from 6.6 g/cc Green Density Powder apparent bulk density 2.8 g/cc; powder flow 30 sec/50g.Compacting properties measured on powders with 1% lithium stearite. Sintering was done in dissociated ammonia at 1121°C (2050°F) for .. |
|||
Tensile Strength, Ultimate | >= 450 MPa | >= 65300 psi | |
AK Steel ASTM A 570, Grade 50 Hot Rolled Carbon Steel, Structural Quality (SQ) For gauges up to 0.229", ASTM A 570 must be specified, gauges >0.230", ASTM A 907 must be used. Items 0.180 to 0.230" gauge which are >48" wide may be ordered to either A 570 or A 907.Information p.. |
|||
Tensile Strength, Ultimate | 450 MPa | 65300 psi | |
AK Steel DI-MAX® HF-10 Nonoriented Electrical Steel DI-MAX HF-10 is a fully processed nonoriented electrical steel designed for use in high speed motors, traction motors, aircraft generators, and other rotating equipment operating at frequencies abov.. |
|||
Tensile Strength, Ultimate | >= 450 MPa | >= 65300 psi | Minimum |
Aleris Hokotol Aluminum Alloy, 325 mm Thickness Sample treatment not specified for property data.Applications include molds for blow forming and injection molding for plastics; bolsters and force plates; high strength/low weight machine parts; an.. |
|||
Tensile Strength, Ultimate | 450 - 520 MPa | 65300 - 75400 psi | |
ArcelorMittal HSLA 360 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S355MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w.. |