Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 435 MPa @Temperature 500 °C |
63100 psi @Temperature 932 °F |
EN min.; EN 10002-5 |
Outokumpu 153MA™ High Temperature Austenitic Stainless Steel Variant of 1.4301 with increased silicon and nitrogen contents and microalloyed with rare earth metals (REM). This raises the max service temperature in dry air to 1000°C.Applications: Heat and cr.. |
|||
Tensile Strength, Ultimate | 435 MPa @Temperature 400 °C |
63100 psi @Temperature 752 °F |
EN min.; EN 10002-5 |
Outokumpu 4429 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), cold rolled strip/sheet and rod forms. |
|||
Tensile Strength, Ultimate | >= 435 MPa | >= 63100 psi | |
MetalTek MTEK 20-25 Cast UNS J94213 Heat Resistant Stainless Steel Provides strength levels of HT with better ductility.Applications: Furnace skids for slabs, bars, furnace fixturesInformation provided by MetalTek |
|||
Tensile Strength, Ultimate | >= 435 MPa | >= 63100 psi | |
MetalTek MTEK 20-32Nb Cast UNS N08151 Heat Resistant Stainless Steel Information provided by MetalTek |
|||
Tensile Strength, Ultimate | >= 435 MPa | >= 63100 psi | |
MetalTek MTEK Super 20-32Nb Cast UNS N08151 Heat Resistant Stainless Steel Information provided by MetalTek |
|||
Tensile Strength, Ultimate | 435 MPa @Temperature 871 °C |
63100 psi @Temperature 1600 °F |
|
Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Tensile Strength, Ultimate | 435 MPa | 63100 psi | Typical |
Materion AlBeMet® AM 162 Rolled Sheet, Annealed Mechanical properties are typical, longitudinal values at RT. AlBeMet® AM 162 is a powder metallurgical product produced by gas atomization available as rod, bar, tube and sheet. These shapes are.. |