Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PP 1383 PRE-ELEC PP 1383 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM D638 |
North Wood Plastics PS with 60% Wood Fiber Data provided by North Wood Plastics, Inc. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ISO 527 |
Eastman EASTALLOY Polymer DA003-8999K, Clear Alloy
(discontinued **) Properties below based on a film thickness of 250 microns. CO2 Permeability is 49 cm3·mm/m2·24h·atm per ASTM D 1434.Product Description: EASTALLOY DA003-8999K Polymer is a clear copolyester/pol.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM Data |
Americas Styrenics Styron® XL-8023VC High Impact Polystyrene
(discontinued **) STYRON® XL-8023 VC high impact polystyrene is designed to provide molders of VCR cassettes with the impact and gloss they require, at economics and processability highly advantaged over ABS resins... |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM D638 |
NOVA Chemicals Novapol® HB-Y556-A HDPE Extrusion Resin
(discontinued **) Molded Plaque Properties. Features: Excellent ESCR, high rigidity and impact strength, good melt strength.Applications: chemical bottles, toys, blend for use with post-consumer resins.Data provided.. |
|||
Tensile Strength, Ultimate | 28.0 MPa @Thickness 1.60 mm |
4060 psi @Thickness 0.0630 in |
Sintered moldings; ASTM D4894/4895 |
3M Dyneon™ TF 2024 PTFE Paste Extrusion Powder
(discontinued **) Type I PTFE. Free flowing powder. Minimum reduction ratio is 20; Max is 500. Average particle size 500µm. Used for unsintered tapes and sealing cords.Dyneon offers a family of PTFE fine powder .. |
|||
Tensile Strength, Ultimate | 28.0 MPa @Thickness 1.60 mm |
4060 psi @Thickness 0.0630 in |
Sintered moldings; ASTM D4894/4895 |
3M Dyneon™ TF 2025 PTFE Paste Extrusion Powder
(discontinued **) Type I PTFE. Free flowing powder. Minimum reduction ratio is 20; Max is 300. Average particle size 500µm. Used for liners.Dyneon offers a family of PTFE fine powder paste extrusion resins. Thes.. |
|||
Tensile Strength, Ultimate | 28.0 MPa @Thickness 1.60 mm |
4060 psi @Thickness 0.0630 in |
Sintered moldings; ASTM D4894/4895 |
3M Dyneon™ TF 2029 PTFE Paste Extrusion Powder
(discontinued **) Type I PTFE. Free flowing powder. Minimum reduction ratio is 5; Max is 100. Average particle size 500 µm. Used for electrical insulating tapes, liners, and yarns.Dyneon offers a family of PTFE .. |
|||
Tensile Strength, Ultimate | 28.0 MPa @Thickness 1.60 mm |
4060 psi @Thickness 0.0630 in |
Sintered moldings; ASTM D4894/4895 |
3M Dyneon™ TF 2071 PTFE Paste Extrusion Powder
(discontinued **) Type I PTFE. Free flowing powder. Minimum reduction ratio is 20; Max is 1600. Average particle size 500 µm. Used for tubing, wire/cable insulation, 'spaghetti tubing' production.Dyneon offers a.. |
|||
Tensile Strength, Ultimate | 28.0 - 116 MPa @Temperature -40.0 - 80.0 °C |
4060 - 16800 psi @Temperature -40.0 - 176 °F |
Average value: 73.0 MPa Grade Count:2 |
Overview of materials for Nylon 66, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | Compounded Tire |
Polychloroprene Rubber (CR) Polychloroprene rubber usually withstands ozone, oli/fat/grease, and many solvents. It is impacted by esters, ketones, chlorinated solvents, aromatic hydrocarbons, strong oxidizing acids, and nitro.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | Compounded Tire |
Natural Rubber, Vulcanized (NR, IR, Polyisoprene) Natural rubber is polyisoprene. Chemical and environmental resistance and mechanical properties are improved through crosslinking (vulcanizing), usually through treatment with sulfur.Natural rubber.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | |
Kuraray HYBRAR® PH8 Polypropylene Blend Description: HYBRAR® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRAR® is a special thermoplastic rubb.. |
|||
Tensile Strength, Ultimate | 28.0 MPa @Temperature -20.0 °C |
4060 psi @Temperature -4.00 °F |
Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 |
DuPont Elvax® 450 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 397 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 397 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | DIN 53504 |
Lubrizol ESTANE® 58300 Ether Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | DIN 53504 |
Lubrizol ESTANE® 58866 Ether Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ISO 37 |
Lubrizol ESTANE® GP65AE Ester Based Thermoplastic Polyurethane Type: Estane® GP 65AE is an aromatic polyester-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding partsAvailable in EuropeInformation provided b.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 397 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM D638 |
Lubrizol Estaloc® 59020 Reinforced Thermoplastic Polyurethane Type: Estaloc® 59020 RETPU is a polyester-type reinforced engineered thermoplastic polyurethane (RETPU).Features: Fast cycling, dimensional stability, durability, aesthetics, low temperature impact.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM D638/D412 |
Covestro Bayflex® 110-35 IMR Polyurethane Elastomeric RIM, 18% Mineral Filled, MDI-based 2-Component Liquid System Calcium Silicate filled. 0.15 in. thickness. IMR=Internal Mold Release RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Ba.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM D638/D412 |
Covestro Bayflex® 180 Polyurethane Elastomeric RIM, 20% Mineral Filled, MDI-based 2-Component Liquid System 0.1 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and offi.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM D638/D412 |
Covestro Bayflex® 180 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and o.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ISO 527 |
DSM Fibre Intermediates Nyrim® 1525 (Glass), Conditioned Conditioned at 23°C and 50% Relative Humidity.Nyrim is a Block Copolymer of Nylon 6 and an elastomer with exceptional properties in impact resistance, fatigue and abrasion resistance. Nyrim is proc.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | Dynamic tensile strength |
Channel Industries 5500 Lead Zirconate Titanate Piezoelectric Navy Type IICharacterized by high coupling factors and high piezoelectric and dielectric constants over extended temperature ranges and stress amplitudes, lead zirconate titanates are the most exten.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | Dynamic tensile strength |
Channel Industries 5600 Lead Zirconate Titanate Piezoelectric Navy Type VCharacterized by high coupling factors and high piezoelectric and dielectric constants over extended temperature ranges and stress amplitudes, lead zirconate titanates are the most extens.. |
|||
Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM D412-80 |
DuPont Performance Polymers Hypalon® 40 Chlorosulfonated Polyethylene Rubber, Gum Compound
(discontinued **)& Gum compound with 100 parts Hypalon; 4 parts high activity magnesia; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont Dow Elastomers). Reinforcing fillers not needed.. |