Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 26.5 - 45.0 MPa | 3840 - 6530 psi | Average value: 35.7 MPa Grade Count:63 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant". Each property range of values rep.. |
|||
Tensile Strength, Ultimate | 26.5 - 41.4 MPa | 3840 - 6000 psi | Average value: 35.1 MPa Grade Count:4 |
Overview of materials for ABS/Polyester Alloy This property data is a summary of similar materials in the MatWeb database for the category "ABS/Polyester Alloy". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
Tensile Strength, Ultimate | 26.5 MPa | 3840 psi | ASTM D638 |
KKPC Kuhmo HF 402 Flame Retarded General Purpose HIPS Key features: Good mechanical balance, High Strength. Common Uses: Parts needing strength.HIPS is a functional resin made by copolymerization of styrene monomer and PBR. It shows excellent balance b.. |
|||
Tensile Strength, Ultimate | 26.5 MPa | 3840 psi | 150°C, 40 min., Pressure Vulcanization. -1% Change after 100°C, 70 hrs, Oil Immersion |
KKPC KOSYN KNB 40M Acrylonitrile Butadiene Rubber (NBR) Acrylonitrile Butadiene Rubber (NBR)Characteristics: KOSYN KNB is copolymer of high oil resistance and chemical resistance made from acrylonitrile and butadiene by the cold emulsion polymerization. .. |
|||
Tensile Strength, Ultimate | 26.5 MPa | 3840 psi | ASTM D638 |
KKPC Kuhmo HI 425TVD High Flow/High Heat Resistant HIPS Key features: High-impact-fluidity. Common Uses: TV cover, computer case.HIPS is a functional resin made by copolymerization of styrene monomer and PBR. It shows excellent balance between impact-res.. |
|||
Tensile Strength, Ultimate | 26.5 MPa | 3840 psi | ASTM D638 |
SK Chemicals SKYPEL G140D General Grade SKYPEL is a thermoplastic polyester elastomer (TPEE). It is a polymer resin having the property somewhere between plastics and rubber, which have various properties ranging from high hardness plasti.. |
|||
Tensile Strength, Ultimate | 26.5 MPa | 3840 psi | ASTM D638 |
Samyang Triel® 5552EM Thermoplastics Polyetherester Elastomer, Extrusion Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5552EM is an extrusion grade.Information provided by Samyang. |
|||
Tensile Strength, Ultimate | 26.5 MPa @Temperature 260 °C |
3840 psi @Temperature 500 °F |
ASTM D1708 |
Daelim H&L Plavis-G40 DF 40% Graphite Filled Aromatic Polyimide Bearing Direct Formed. Plavis-G-40: Graphite 40 wt% filled, Self lubricating grade with low thermal expansion.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 carbons is.. |
|||
Tensile Strength, Ultimate | 26.5 MPa | 3850 psi | after optimum cure |
Armstrong C-7/W Epoxy Adhesive, 2:3 Mix Ratio A clear, unfilled, medium viscosity adhesive recommended for use with any Armstrong Activator. Physical property data included covers C-7 used with Activators W and H-20. All other Activators may .. |
|||
Tensile Strength, Ultimate | 26.5 MPa | 3850 psi | after optimum cure |
Armstrong X-81/A Epoxy Adhesive Information provided by Ellsworth Adhesives. |
|||
Tensile Strength, Ultimate | 26.5 MPa | 3840 psi | ASTM D638 |
Samyang Triel® 5550 Thermoplastics Polyetherester Elastomer, General Extrusion Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5550 is an extrusion grade.Information provided by Samyang. |