Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 17.3 MPa @Thickness 3.17 mm |
2510 psi @Thickness 0.125 in |
Type IV specimen, 2" per minute test speed, rotomolded samples; ASTM D638 |
NOVA Chemicals Novapol® TR-0735-U Hexene MDPE Rotational Molding Resin Good impact resistance, Excellent processabilityApplications: Toys, Complex custom parts, Home and garden items, MailboxesAdditives: Processing antioxidants, UV stabilizersInformation provided by NO.. |
|||
Tensile Strength, Ultimate | 17.3 MPa @Thickness 3.17 mm |
2510 psi @Thickness 0.125 in |
Type IV specimen, 2" per minute test speed, rotomolded samples; ASTM D638 |
NOVA Chemicals Novapol® PR-0636-UG Butene MDPE Rotational Molding Resin
(discontinued **) Very good processability, Very good ESCR, Good impact properties, NSF listed for Stds. 14, 24, and 61Applications: Toys, General purpose custom molding, Carts, Playground equipmentAdditives: Process.. |
|||
Tensile Strength, Ultimate | 17.3 MPa @Thickness 3.17 mm |
2510 psi @Thickness 0.125 in |
Type IV specimen, 2" per minute test speed, rotomolded samples; ASTM D638 |
NOVA Chemicals Sclair® TD-7915-UG Hexene MDPE Rotational Molding Resin
(discontinued **) Excellent low temperature impact properties, Excellent ESCR, Wide process window, NSF listing for Stds. 14, 24, and 61 pending, Retention of impact at long cook timesApplications: IBCs, Toys, Genera.. |
|||
Tensile Strength, Ultimate | 17.3 MPa | 2500 psi | ASTM D412 |
Stellarchem SV-B40D TPV Compound This grade of Stellarchem SV series is a dynamic crosslinked, EPDM/PP compound. It's design to replace thermoset elastomers, such as EPDM, and traditional Thermoplastic TPVs. It can be process on .. |
|||
Tensile Strength, Ultimate | 17.3 MPa | 2510 psi | |
DuPont Vamac® GXF Sample Compound Vulcanizate Slab Cure (5 minutes at 190°C) Without Armeen® 18D Test slab is cured for 5 minutes at 190°C and post cured for 4hrs at 175°C. Vulcanizate performance test data can help end-users evaluate the potential fitness of similar compounds for their own .. |
|||
Tensile Strength, Ultimate | 17.3 MPa @Thickness 3.17 mm |
2510 psi @Thickness 0.125 in |
Type IV specimen, 2" per minute test speed, rotomolded samples; ASTM D638 |
NOVA Chemicals Sclair® TD-7915-U Hexene MDPE Rotational Molding Resin
(discontinued **) Excellent low temperature impact properties, Excellent ESCR, Wide process window, NSF listing for Stds. 14, 24, and 61 pending, Retention of impact at long cook timesApplications: IBCs, Toys, Genera.. |
|||
Tensile Strength, Ultimate | 17.3 MPa @Thickness 3.17 mm |
2510 psi @Thickness 0.125 in |
Type IV specimen, 2" per minute test speed, rotomolded samples; ASTM D638 |
NOVA Chemicals Novapol® PR-0636-U Butene MDPE Rotational Molding Resin
(discontinued **) Very good processability, Very good ESCR, Good impact properties, NSF listed for Stds. 14, 24, and 61Applications: Toys, General purpose custom molding, Carts, Playground equipmentAdditives: Process.. |