Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 11.7 - 13.8 MPa | 1700 - 2000 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO 1047 (AH) The burn rate is 0.53 in/min; ASTM FM VSS 302.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 11.7 - 15.1 MPa | 1700 - 2190 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO DEFA 1047 The burn rate is 0.53 in/min; ASTM FM VSS 302.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | TM R050-36 |
Resinlab® EP1112NC Clear Electronic Grade Epoxy Encapsulant Resinlab™ EP1112NC Clear is a two part unfilled fast curing electronic grade epoxy encapsulant designed for small to medium sized castings. EP1112NC Clear is a modified version of the standard EP11.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | TM R050-36 |
Resinlab® EP1112NC Black Electronic Grade Epoxy Encapsulant Resinlab™ EP1112NC Black is a two part unfilled fast curing electronic grade epoxy encapsulant designed for small to medium sized castings. EP1112NC Black is a modified version of the standard EP11.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman 1830A Polyethylene
(discontinued **) Polyethylene 1830A is a low density formulation. It is suggested for injection molding applications requiring good stiffness or gloss properties . It us used in applications such as closures.Polyet.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman 1830E Polyethylene
(discontinued **) Polyethylene 1830E is a low density formulation. It is suggested for general purpose extrusion applications, such as tubing and blow molding. Polyethylene 1830E meet the requirements of FDA regula.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman E6838-862A Polyethylene
(discontinued **) E6838-862A is a low density formulation suggested for injection molding applications, such as closuresInformation supplied by the manufacturer.Information from manufacturer data sheet.Eastman Chemic.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | ASTM D638 |
ExxonMobil Escorene® LD-401 EVA for Electrical Insulation
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A crosslinkable, 9.9% vinyl acetate copolymer designed for electrical applications.Applications: Base resin for fully formulated low voltage cable i.. |
|||
Tensile Strength, Ultimate | 11.7 - 44.0 MPa | 1700 - 6380 psi | Average value: 30.1 MPa Grade Count:80 |
Overview of materials for High Density Polyethylene (HDPE), Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Blow Molding Grade". Each property range of values reported is minimum.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | ASTM D638 |
Multibase Multi-Flex® D 3204 TPE Thermoplastic Elastomer Features: Chemical Resistance, Good Colorability, GoodElasticity, HighElectrically InsulatingFlame RetardantFlexibility, GoodHeat StabilizedOzone ResistantProcessability, GoodUV Resistance, Good P.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | |
Sylvin Technologies 8980-75 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | |
Sylvin Technologies 9077-95 LMW Natural PVC for Injection Molding Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | |
Sylvin Technologies 9980-75 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | |
Sylvin Technologies 9999-95 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | Heat aged 2 weeks at 175°C |
DuPont Vamac® DP Sartomer 350 Coagent Test Compound Vamac® DP is an ethylene acrylic dipolymer elastomer. Its general performance characteristics are similar to those of the Vamac® terpolymers, including:Good oil and chemical resistanceHigh temper.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | Cecilia 20 aged 168 hrs at 175°C |
DuPont Vamac® DP Activator OC Coagent Test Compound Vamac® DP is an ethylene acrylic dipolymer elastomer. Its general performance characteristics are similar to those of the Vamac® terpolymers, including:Good oil and chemical resistanceHigh temper.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | 508 mm/min; ASTM D638 |
Dow Engage® ENR 7256.00 Ethylene-Butene Copolymer Description: ENR 7256.00 is a unique broader molecular weight distribution ethylene-butene copolymer with higher branching levels that offers excellent clarity, processing and performance in foams a.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | ASTM D638 |
Colorite Polymers 6077 Non-Phthalate 77 Series Vinyl Compound Description: The Colorite 77 series is a family of compounds designed for those medical device producers that require the use of a non-phthalate plasticizer that has superior resistance to extractio.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | |
Colorite Polymers 6511 Clear Extrusion Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for the extrusion of various components for the production of devices. The vinyl components used in pre.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | |
Colorite Polymers 6512 Clear Injection Molding Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for injection molding of various components such as drip chambers, connectors, valves, etc. The vinyl c.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | |
Colorite Polymers Self Frosting™ 6511SF Vinyl Compound Description: Colorite has developed a family of vinyl compounds to satisfy the needs of those who need a smooth, low gloss, low friction surface for the products that they produce. Historically, thi.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | ASTM D412; ISO 37; DIN 53504 |
Advanced Polymer Alloys Alcryn® 2165 NC Melt Processable Rubber Alcryn 2100 Series melt-processable rubber (MPR) offer a broader range of bonding to rigid substrates while maintaining all the excellent performance features of traditional Alcryn. The 2100 grades.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | ASTM D638 |
Colorite Polymers 6575 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 11.7 - 20.7 MPa | 1700 - 3000 psi | Average value: 16.1 MPa Grade Count:7 |
Overview of materials for Linear Low Density Polyethylene (LLDPE), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE), Extrusion Grade". Each property range of values reported is min.. |
|||
Tensile Strength, Ultimate | 11.7 - 27.1 MPa | 1700 - 3930 psi | Average value: 19.5 MPa Grade Count:10 |
Overview of materials for Linear Medium Density Polyethylene (LMDPE), Rotational Molded This property data is a summary of similar materials in the MatWeb database for the category "Linear Medium Density Polyethylene (LMDPE), Rotational Molded". Each property range of values reported i.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | Across Flow; ASTM D412 |
ExxonMobil Santoprene® 123-50 Thermoplastic Elastomer
(discontinued **) A hard, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide ran.. |
|||
Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | Bond strength to metal |
Dymax Light Weld® 429 High Clarity Glass Bonding Adhesive Glass Bonding in SecondsDescriptionDymax Light Weld® 400 Series adhesives form high-clarity, invisible bonds between glass and other substrates in seconds. In addition to many structural glass bond.. |