Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 400 MPa @Temperature 25.0 °C |
58000 psi @Temperature 77.0 °F |
|
MarkeTech Sapphire (Aluminum Oxide - Al2O3) Single Crystal Data provided by the supplier, MarkeTech International.Sapphire is grown by several methods: Boule form (Czochralski), in plate form, or as tubes, rods and plates. Boules are grown up to 8" diam.. |
|||
Tensile Strength | 400 MPa @Diameter 25.0 - 50.0 mm |
58000 psi @Diameter 0.984 - 1.97 in |
|
United Cast Bar Unibar 400-15 As Cast Continuously Cast Spheroidal Graphite Iron Offers superior machinability combined with good impact, fatigue, electrical conductivity and magnetic permeability. Noise and vibration damping are good in this grade.Unibar 400-15 is not recommend.. |
|||
Tensile Strength | 400 MPa @Diameter 25.0 - 50.0 mm |
58000 psi @Diameter 0.984 - 1.97 in |
|
United Cast Bar Unibar 400-15 Fully Annealed Continuously Cast Spheroidal Graphite Iron Offers superior machinability combined with good impact, fatigue, electrical conductivity and magnetic permeability. Noise and vibration damping are good in this grade.Unibar 400-15 is not recommend.. |
|||
Tensile Strength | 400 MPa @Temperature 100 °C |
58000 psi @Temperature 212 °F |
|
Magnesium Elektron Elektron® 675 Magnesium Wrought Alloy High strength wrought Mg alloy used for high performance components, including at elevated temperature. Excellent corrosion resistance and easily machined. Can be extruded, forged and hot formed. .. |
|||
Tensile Strength | >= 400 MPa @Thickness 127 - 152.4 mm |
>= 58000 psi @Thickness 5.00 - 6.000 in |
Tempers T651 / T652 |
Constellium Alumold® 400 Aluminum The Alumold®-400 alloy has been optimized to provide good shape stability and high strength properties throughout the plate thickness. Typical applications include blow moulds, thermoforming moulds.. |
|||
Tensile Strength | 400 MPa @Thickness 254 - 305 mm |
58000 psi @Thickness 10.0 - 12.0 in |
Typical Strength |
Constellium Alumold® 400 Aluminum The Alumold®-400 alloy has been optimized to provide good shape stability and high strength properties throughout the plate thickness. Typical applications include blow moulds, thermoforming moulds.. |
|||
Tensile Strength | >= 400 MPa @Thickness 15.0 - 35.0 mm |
>= 58000 psi @Thickness 0.591 - 1.38 in |
Temper T651 |
Constellium Unidal® High-Strength Rolled Precision Aluminum Plate, Milled Both Sides Unidal® precision plates offers a combination of dimensional stability and high mechanical strength. The very low internal stress reduces the risk of deformation during machining, thereby reducing .. |
|||
Tensile Strength | >= 400 MPa @Thickness 35.0 - 60.0 mm |
>= 58000 psi @Thickness 1.38 - 2.36 in |
Temper T651 |
Constellium Unidal® High-Strength Rolled Precision Aluminum Plate, Milled Both Sides Unidal® precision plates offers a combination of dimensional stability and high mechanical strength. The very low internal stress reduces the risk of deformation during machining, thereby reducing .. |