Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	792 MPa @Temperature 25.0 Â°C	115000 psi @Temperature 77.0 Â°F
Haynes 75 Nickel Alloy Sheet, Annealed at 1925Â°F (1050Â°C) Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200Â°F (650Â°C). It is principally used in low stress elevated temperature applications requiring reas..
Tensile Strength, Ultimate	791 MPa @Thickness 12.7 mm, Temperature 25.0 Â°C	115000 psi @Thickness 0.500 in, Temperature 77.0 Â°F	as welded
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate	791 MPa @Thickness 9.50 mm, Temperature 20.0 Â°C	115000 psi @Thickness 0.374 in, Temperature 68.0 Â°F
Haynes HastelloyÂ® C-4 alloy, plate, heat treated at 1066Â°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Tensile Strength, Ultimate	793 MPa @Temperature 399 °C	115000 psi @Temperature 750 °F	Round bar 1" diameter, 310 HB
EDRO #2 Prehardened 4130 Holder Block EDRO #2™ is a vacuum-degassed Chromium-Molybdenum-alloyed steel which is supplied in the hardened and tempered condition. EDRO #2™ is characterized by excellent machinability, good resistance to i..
Tensile Strength, Ultimate	793 MPa @Temperature 399 °C	115000 psi @Temperature 750 °F	Round bar 1" diameter, 310 HB
EDRO #3 Prehardened Mold Quality P20 Alloy Steel EDRO #3™ is a vacuum-degassed, ladle refined, Cr-Ni-Mo- alloyed steel which is supplied in the hardened and tempered condition. EDRO #3™ is manufactured to consistently high quality standards with..
Tensile Strength, Ultimate	790 MPa @Thickness 3.20 mm, Temperature 20.0 °C	115000 psi @Thickness 0.126 in, Temperature 68.0 °F
Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Tensile Strength, Ultimate	795 MPa @Thickness 12.7 mm, Temperature 93.0 °C	115000 psi @Thickness 0.500 in, Temperature 199 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe..