Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 1120 MPa @Temperature 540 °C |
162000 psi @Temperature 1000 °F |
|
Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750) Haynes X-750 (UNS No. N07750) alloy is an age-hardenable, nickel-base superalloy with very good strength at temperatures up to about 1600°F (870°C). It is widely used as a wrought material for.. |
|||
Tensile Strength, Ultimate | 1120 MPa @Thickness 12.7 mm, Temperature 25.0 °C |
162000 psi @Thickness 0.500 in, Temperature 77.0 °F |
As Welded and Aged at 1850°F(1010°C)/2hr/AC + 1450°F(788°C)/8h/AC; Weld/Weld Fracture |
Haynes 282® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Tensile Strength, Ultimate | 1120 MPa @Temperature 550 °C |
162000 psi @Temperature 1020 °F |
Precipitation Hardened prior to test |
Special Metals INCONEL® Alloy X-750 A nickel-chromium alloy similar to INCONEL alloy 600 but made precipitation hardenable by additions of aluminum and titanium. The alloy has good resistance to corrosion and oxidation along with hig.. |
|||
Tensile Strength, Ultimate | 1120 MPa @Thickness 25.4 mm, Temperature 25.0 °C |
162000 psi @Thickness 1.00 in, Temperature 77.0 °F |
Welded then age-hardened |
Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl.. |