Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 248 MPa | 36000 psi | ASTM D790 |
Performance Polymers IPS II PPL-C4219 PEKK (Polyetherketoneketone) Linear Wear Grade Black pellets; Carbon fiber/PTFE/Graphite compoundInformation provided by Infinite Polymer System II. |
|||
Flexural Yield Strength | 248 MPa | 36000 psi | ASTM D790 |
Techmer ES Plaslube® J-1/30/SI/2 Nylon 66, 30% GFR, 2% Silicone Plaslube silicone lubricated nylon 66 grades are cost-effective wear and friction materials with low coefficients of friction. These grades have a potential for noise reduction due to the migratory.. |
|||
Flexural Yield Strength | 248 MPa | 36000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP OF008A PPS (Asia Pacific) LNP* Thermocomp* OF008A is a compound based on PPS - Branched resin containing Glass Fiber.This product is also known as Thermocomp* OF-1008. |
|||
Flexural Yield Strength | 248 MPa | 36000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA 30% Glass Reinforced PPE+PA Alloy. |
|||
Flexural Yield Strength | 248 MPa | 36000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA (Asia Pacific) GR 30%. Highest stiffness of 1200000 psi (8200 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: under the bonnet. |
|||
Flexural Yield Strength | 248 MPa | 36000 psi | ASTM D790 |
Clariant Renol 60G33HSL Nylon 6, 33% Glass Fiber Reinforced, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 248 MPa | 36000 psi | ASTM D790 |
Clariant Renol 60G33-L Nylon 6, 33% Glass Fiber Reinforced, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 248 MPa | 36000 psi | ASTM D790 |
Clariant Renol PA113G33HR Nylon 66, 33% Glass Fiber, Heat Stabilized, Hydrolysis Resistant Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 248 MPa | 36000 psi | ASTM D790 |
Clariant Renol PA213G30 Nylon 6, 30% Glass Fiber, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 248 MPa | 36000 psi | ASTM D790 |
Clariant Renol PA213G33 Nylon 6, 33% Glass Fiber, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 248 MPa | 36000 psi | ASTM D790 |
Clariant Renol PA213G36S Nylon 6, 36% Glass Fiber, Heat Stabilized, Silicone Lubricated Data provided by Clariant Masterbatches |