Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 221 MPa | 32100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers UTTAP SF 50030GF Polyethersulfone, 30% Glass Reinforced Glass reinforced (30 %) Polyether Sulfone, excellent chemical and electrical resistance, high stiffness, modulus and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50%.. |
|||
Flexural Yield Strength | 221 MPa | 32100 psi | ASTM D790 |
PolyOne Edgetek® ES-40GF/000 Polyethersulfone - 40% Glass Fiber Reinforced
(discontinued **) Data provided by PolyOne. |
|||
Flexural Yield Strength | 221 MPa | 32100 psi | ASTM D790 |
Chem Polymer Chemlon 233 GVH Nylon 6, 33% Glass Fiber Reinforced A glass fiber reinforced, flame retardant nylon 6, exhibiting excellent tensile strength and stiffness. The material has V0 flammability rating according to UL 94 testing procedure at thickness dow.. |
|||
Flexural Yield Strength | 221 MPa | 32100 psi | ASTM D790 |
PolyOne Edgetek® NI-30GF/000 Nylon 6/10 - 30% Glass Fiber Reinforced
(discontinued **) Data provided by PolyOne. |
|||
Flexural Yield Strength | 221 MPa | 32100 psi | (102 mm Span) 3mm/min; ASTM D790 |
LNP ULTEM® SMU5834 Polyetherimide, 20% Carbon Fiber Reinforcement
(discontinued **) High modulus with shielding/ conductive characteristics for high-heat applications.Features: Electrically Conductive, High Heat Resistance, High StrengthForms: PelletsProcessing Method: Injection Mo.. |