Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 153 MPa | 22200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 3413HF PC (Asia Pacific) 30% glass reinforced, high flow PC. |
|||
Flexural Yield Strength | 153 MPa | 22200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 3413R PC 30% GR, provides improved mechanical properties and UL94V-1 rated at 0.058"". Internal mold release added. |
|||
Flexural Yield Strength | 153 MPa | 22200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 3413R PC (Asia Pacific) Lexan* resin 3413R is a flame retardant polycarbonate grade with 30% glass fiber reinforcement to meet UL 94 V1 listing at 1.5mm. This grade can be considered for applications requiring higher stiff.. |
|||
Flexural Yield Strength | 153 MPa | 22200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL34XXP PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL-4034 HP is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |
|||
Flexural Yield Strength | 153 MPa | 22200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 3413HF PC 30% glass reinforced, high flow PC. |
|||
Flexural Yield Strength | 153 MPa | 22200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Lubricomp JX91055 PES (Europe-Africa-Middle East) LNP* LUBRICOMP* JX91055 is a compound based on Polyethersulfone resin containing Carbon Fiber and Proprietary Lubricant . Added features include Internally Lubricated and Electrically Conductive.Thi.. |
|||
Flexural Yield Strength | 153 MPa | 22200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP PH0400CX PA 6 LNP* THERMOCOMP* PH0400CX is a compound based on Nylon 6 resin. Added feature of this grade is: High Specific Gravity. |
|||
Flexural Yield Strength | 153 MPa | 22200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP PH0400CX_BK1D466 PA 6 4.0 specific gravity, Nylon 6 |
|||
Flexural Yield Strength | 153 MPa | 22200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP VERTON MV00ES PP LNP* VERTON* MV00ES is primarily a concentrate used for blending purposes. This is a 70% long glass fiber Polypropylene compound. Added features of this grade are: Heat Stabilized |
|||
Flexural Yield Strength | 153 MPa | 22200 psi | ASTM D790 |
Techmer ES HiFill® PSU GF20 BK 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc. |