Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | >= 0.140 GPa | >= 20.3 ksi | 2% sec, TD; ASTM D882 |
NIZHNEKAMSKNEFTEKHIM PE 4117N (18401) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Tensile Modulus | >= 0.140 GPa | >= 20.3 ksi | 2% sec, TD; ASTM D882 |
NIZHNEKAMSKNEFTEKHIM PE 4118N (18401) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Tensile Modulus | >= 0.140 GPa | >= 20.3 ksi | 2% sec, TD; ASTM D882 |
NIZHNEKAMSKNEFTEKHIM PE 5117N (18601) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Tensile Modulus | >= 0.140 GPa | >= 20.3 ksi | 2% sec, TD; ASTM D882 |
NIZHNEKAMSKNEFTEKHIM PE 5117P (18602) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Tensile Modulus | >= 0.140 GPa | >= 20.3 ksi | 2% sec, TD; ASTM D882 |
NIZHNEKAMSKNEFTEKHIM PE 5118N (18601) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Tensile Modulus | >= 0.140 GPa | >= 20.3 ksi | 2% sec, TD; ASTM D882 |
NIZHNEKAMSKNEFTEKHIM PE 5118P (18602) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Tensile Modulus | >= 0.140 GPa | >= 20.3 ksi | 2% sec, TD; ASTM D882 |
NIZHNEKAMSKNEFTEKHIM PE 4117P (18402) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Tensile Modulus | >= 0.140 GPa | >= 20.3 ksi | 2% sec, TD; ASTM D882 |
NIZHNEKAMSKNEFTEKHIM PE 4118P (18402) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Tensile Modulus | >= 0.140 GPa | >= 20.3 ksi | in the plane; ISO 527 1-2 |
3A Composites Core Materials AIREX® C70.200 Universal Structural Foam AIREX® C70 is a closed cell, crosslinked polymer foam that combines excellent stiffness and strength to weight ratios with superior toughness. It is non-friable, contains no CFC’s, has negli.. |
|||
Tensile Modulus | 0.140 GPa | 20.3 ksi | |
Kuraray HYBRAR® PH4 Polypropylene Blend Description: HYBRAR® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRAR® is a special thermoplastic rubb.. |
|||
Tensile Modulus | 0.140 GPa | 20.3 ksi | |
Kuraray HYBRAR® PH7 Polypropylene Blend Description: HYBRAR® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRAR® is a special thermoplastic rubb.. |
|||
Tensile Modulus | 0.140 GPa | 20.3 ksi | Bending Modulus; ASTM D790 |
UBE UMERIT 500F Metallocene LLDPE Description: UBE Super Polyethylene Umerit® is an ethylene-olefin copolymer made by UBE using the metallocene catalytic method. The metallocene catalytic method results in superior physical propert.. |
|||
Tensile Modulus | 0.140 GPa | 20.3 ksi | ISO 527-1/-2 |
DuPont Performance Polymers Hytrel® HTR8068 Polyester Elastomer TPC-ET
(Unverified Data**) 44 Shore D Flame Retardant Polyester Elastomer Developed for Extrusion and Injection Molding Information provided by DuPont Performance Polymers |
|||
Tensile Modulus | 0.140 GPa | 20.3 ksi | 1 mm/min |
Arkema Group Evatane® 1003 VL 2 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Anti-UV stabilized grade. Applications Thermal and colorless agricultural film to 180 at 200 µ for greenhouse coverage.ISO data provided by the .. |
|||
Tensile Modulus | 0.140 GPa | 20.3 ksi | 1 mm/min |
Arkema Group Evatane® 1005 VN 2 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process.Applications Grade for transparent and resistant film production. Examples: curtain stretch, coextrusion, stretch hood.ISO data provided by the ma.. |
|||
Tensile Modulus | 0.140 GPa | 20.3 ksi | 1 mm/min |
Arkema Group Evatane® 1020 VB 2 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for transparent, resistant films, sealable at low temperature. Examples: laminates.ISO data provided by the manufacturer, Arke.. |
|||
Tensile Modulus | 0.140 GPa | 20.3 ksi | 1 mm/min |
Arkema Group Evatane® 1005 VG 2 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for strength films, sealable at low temperature with some hot tack. Examples: rigid bags, deep-freeze packaging, laminates, co.. |
|||
Tensile Modulus | 0.140 GPa | 20.3 ksi | 1 mm/min |
Arkema Group Evatane® 1006 VL 2E Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Anti-UV stabilized grade. Applications Thermal and colorless agricultural film to 200 at 210 µm for greenhouse coverage.ISO data provided by the.. |
|||
Tensile Modulus | 0.140 GPa | 20.3 ksi | 1 mm/min |
Arkema Group Evatane® 1020 VG 2 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for resistant films, sealable at low temperature with some hot tack. Examples: bags, deep-freeze packaging, laminates, coextru.. |
|||
Tensile Modulus | 0.140 GPa | 20.3 ksi | ISO 527-1/-2 |
DSM Arnitel® CM551 TPC-ES Heat Resistant Copolyester |