Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 680 - 830 MPa | 98600 - 120000 psi | |
Materion Beryllium Copper Alloy 10 Plate & Rolled Bar; HT (TH04) Temper; up to 76 mm Thickness (UNS C17500) Treatment required for max strength: 2 hrs @ 480°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In.. |
|||
Tensile Strength, Yield | 680 - 830 MPa | 98600 - 120000 psi | |
Materion Beryllium Copper Alloy 3 Plate & Rolled Bar; HT (TH04) Temper; up to 76 mm Thickness (UNS C17510) Treatment required for max strength: 2 hrs @ 480°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In.. |
|||
Tensile Strength, Yield | 680 MPa @Strain 0.200 % |
98600 psi @Strain 0.200 % |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Yield | 680 MPa @Strain 0.200 %, Temperature 650 °C |
98600 psi @Strain 0.200 %, Temperature 1200 °F |
|
Haynes 242® alloy, cold rolled sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Tensile Strength, Yield | 680 MPa @Strain 0.200 %, Temperature 650 °C |
98600 psi @Strain 0.200 %, Temperature 1200 °F |
Precipitation Hardened prior to test |
Special Metals NIMONIC® Alloy PE11 A nickel-iron-chromium alloy precipitation hardened by titanium and aluminum and solid-solution strengthened by an addition of molybdenum. It was developed as a high-strength sheet alloy for use at.. |
|||
Tensile Strength, Yield | >= 680 MPa @Thickness >=8.00 mm |
>= 98600 psi @Thickness >=0.315 in |
|
ThyssenKrupp PAS 700 Structural Steel for Cold Forming This Material Specification applies to plates made of low carbon high strength steels with minimum yield strength values between 315 and 700 MPa1) in the thermo mechanically rolled delivery conditio.. |
|||
Tensile Strength, Yield | 680 - 830 MPa | 98600 - 120000 psi | |
ArcelorMittal Complex Phase Steel 800 Very high strength steel, Hot Rolled Steel Available in the following: uncoated (HCT780C) and Extragal®/Galvannealed (HCT780C+Z)Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) prod.. |