Polymer Property : Tensile Strength, Yield = 52900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	365 MPa @Strain 0.200 %	52900 psi @Strain 0.200 %
Haynes HastelloyÂ® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Yield	365 MPa @Diameter 12.7 mm	52900 psi @Diameter 0.500 in
Kaiser 4026 T8 Rod & Bar This alloy is used when high strength with wear and/or galling resistance is required. It can eliminate hard-coat anodizing in some applications. Typical applications include air compressor pistons ..
Tensile Strength, Yield	365 MPa @Strain 0.200 %	52900 psi @Strain 0.200 %
Haynes 556Â® alloy, 0% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Yield	365 MPa @Strain 0.200 %	52900 psi @Strain 0.200 %
Haynes 556Â® alloy, 0% cold reduction, 1010Â°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Yield	365 MPa @Strain 0.200 %	52900 psi @Strain 0.200 %
Haynes 556Â® alloy, 0% cold reduction, 1065Â°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Yield	365 MPa @Strain 0.200 %	52900 psi @Strain 0.200 %
Haynes 625 alloy, 30% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Yield	365 MPa	52900 psi	Open Hole Tension, Hot/Wet
Hexcel® HexPly® M36 180°C (350°F) Curing Epoxy Matrix, Unidirectional Prepreg Laminate (M36/32%/135/HTA) Tenax HTA fiberInformation provided by HexCel
Tensile Strength, Yield	365 MPa @Strain 0.200 %	52900 psi @Strain 0.200 %
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW short arc weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin..