Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 12.1 MPa | 1750 psi | ASTM D412 |
Precision Polymer Engineering V75B Fluoroelastomer Compound Fluoroelastomer Rubber, 66-75 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out: M2HK710, A1-10, B37, B38, EF31, EO78, F14, Z1, where Z1 = compressi.. |
|||
Tensile Strength, Yield | 12.1 MPa | 1750 psi | chs 20 in/min; ASTM D412 |
Network Polymers Softflex® 6500 Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc. |
|||
Tensile Strength, Yield | 12.1 MPa | 1750 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR Suprex Clay Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 12.1 MPa | 1750 psi | Elastic; ASTM D412 |
Multibase Multi-Flex® TEA 4001-65 TPO Thermoplastic Polyolefin Elastomer Forms: PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
Tensile Strength, Yield | >= 12.1 MPa | >= 1750 psi | Stress at Elongation M100; ASTM D412 Method A |
Seals Eastern 7130 Fluorocarbon-Elastomer FKM specially for oil & gas service.Information provided by Seals Eastern, Inc. |
|||
Tensile Strength, Yield | 12.1 MPa | 1750 psi | ASTM D412 |
Teknor Apex APEX® 1700-70 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMFeatures-General Purpose, Low Gloss Uses-Appliance Components, Footwear, FurnitureForms-PelletsProcessing Met.. |
|||
Tensile Strength, Yield | 12.1 MPa | 1750 psi | ASTM D412 |
Teknor Apex APEX® 90-A41R-65-NT Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses- Medical Applications, Tubing, Appearance-ClearForms-PelletsProcessing-ExtrusionInformation provided by.. |
|||
Tensile Strength, Yield | 12.1 MPa | 1750 psi | ASTM D412 |
Vicone High Performance Rubber VicoSeal™ 106C-BK High Performance EPDM Rubber Information provided by Vicone |
|||
Tensile Strength, Yield | 12.1 MPa | 1750 psi | ASTM D-638 |
Axiall 53080A Moldings & Extrusions Flexible PVC General purpose molding grade compound.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 12.1 MPa | 1750 psi | ASTM D-638 |
Axiall 8740 Moldings & Extrusions Flexible PVC General purpose extrusion compound recommended for use in weatherstrips, screen spline, extruded shapes and flexible gaskets.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporatio.. |
|||
Tensile Strength, Yield | 12.1 MPa | 1750 psi | ASTM D-638 |
Axiall 8743 Moldings & Extrusions Flexible PVC A high quality extrusion compound recommended for weatherstrips, extruded shapes and flexible gaskets.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 12.1 MPa | 1750 psi | ASTM D-638 |
Axiall 8747 Moldings & Extrusions Flexible PVC Economical general purpose molding and extrusion compound with good flex whitening resistance especially in darker colors.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation i.. |
|||
Tensile Strength, Yield | 12.1 MPa | 1750 psi | 2 in/min (50 mm/min); ASTM D638 |
Bapolene® 2272 Polyethylene, Injection Grade Bapolene LL2272 is a high flow, narrow molecular weight distribution, linear low density polyethylene injection resin. This resin offers excellent stress cracking resistance, flex life, low tempera.. |
|||
Tensile Strength, Yield | 12.1 MPa | 1750 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR Suprex Clay Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 12.1 MPa | 1750 psi | ASTM D-638 |
Axiall 46234B Flexible PVC Injection molding compound designed for automotive encapsulation applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |