Polymer Property : Tensile Strength, Yield = 1700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	11.7 MPa	1700 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable MA301FA Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield	11.7 - 200 MPa	1700 - 29000 psi	Average value: 27.9 MPa Grade Count:339
Overview of materials for Polystyrene, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Impact Modified". Each property range of values reported is minimum and maximum values of a..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
M. Holland Company LD800 LDPE (discontinued **) Features: High Clarity, High Flow, Narrow Molecular Wt. Dist., Good Processability, Warp ResistantUses: Closure Caps, Drink LidsApprovals: FDA 21 CFR 177.1520(c) 2.2 and ASTM D 1248, I, Class A, Cat..
Tensile Strength, Yield	11.7 MPa	1700 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Iceberg Clay Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	11.7 MPa	1700 psi	ISO 1184-1983E
LyondellBasell Montell 8340 Polybutene-1 Key Features: semi-crystalline low ethylene content random copolymer, miscible with polypropylenes, FDA acceptableApplications: minor additive in a polyethylene peel seal layerMeets FDA requirements..
Tensile Strength, Yield	11.7 MPa	1700 psi	ISO 1184-1983E
LyondellBasell Montell 8640 Polybutene-1 Key Features: semi-crystalline low ethylene content random copolymer, miscible with polypropylenes, FDA acceptableApplications: minor additive in a polyethylene peel seal layerMeets FDA requirements..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
LyondellBasell PetrotheneÂ® GA808091 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 808-091 is a broad molecular weight, linear low density polyethylene resin designed for use as a base resin in wire and cable jacketing. An antioxidant package is added to..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
LyondellBasell PetrotheneÂ® GA808093 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 808-093 is a broad molecular weight, linear low density polyethylene resin designed for use as a wire and cable insulation. An antioxidant package is added to ensure therm..
Tensile Strength, Yield	11.7 MPa	1700 psi	Elastic; ASTM D412
Multibase Multi-FlexÂ® D 4400 TPE Thermoplastic Elastomer Features: Chemical Resistance, Good Colorability, GoodElasticity, HighElectrically InsulatingFlame RetardantFlexibility, GoodHeat StabilizedOzone ResistantProcessability, GoodUV Resistance, Good F..
Tensile Strength, Yield	11.7 MPa	1700 psi	@100% Elongation; ASTM D1414
Greene Tweed FLUORAZÂ® 890 Fluoroelastomer, FEPM Sanitary gaskets made from FluorazÂ® 890 are ideal for use in standard SIP and CIP applications where EPDMs and FKMs fail. While EDPMs and FKMs can provide a deal for extended periods, changes in..
Tensile Strength, Yield	11.7 MPa	1700 psi
Spartech 2850-60 PVC for Regulated Applications Information provided by Spartech
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D412
Teknor Apex APEXÂ® 3201-65 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Automotive Applications, Non-specific Food Applications, General Purpose, Medical Applications, Modeling..
Tensile Strength, Yield	11.7 MPa	1700 psi	Longitudinal
Saint-Gobain NortonÂ® FluorglasÂ® ChemfilmÂ® R167 Extruded Expanded PTFE Film (0.010" thick) Description: Expanded Unsintered Films are used in microwave and coaxial cable applications in which low dielectric constant and high velocities are required. R167-nominal density of 0.7 g/cc. R165-..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D412
Teknor Apex APEXÂ® 3301-65 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses-Automotive Applications, Food Service Applications, General Purpose, Medical Applications, Profiles, To..
Tensile Strength, Yield	11.7 MPa	1700 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR Atomite Whiting Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LDPE LD 101BA Wire & Cable Low Density Polyethylene Resin Product Description: LD 101BA Wire & Cable is anon-stabilized LDPE, designed for the production of Medium/High Voltage insulation using the direct peroxide addition. For cleanliness reasons, the mat..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LL 6201.19 Injection Molding Resin Product Description: LL 6201 is a narrow molecular weight butane copolymer designed for applications that require excellent toughness. This resin offers easy processability for applications that req..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LLDPE LL 1001XV Wire & Cable Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 1001 XV is a C4 Ziegler Natta LLDPE for power cable and Telecom jacketing. The grade contains a low level of antioxidants and has excellent Environmental Stress Crack Resista..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LLDPE LL 1002YB Wire & Cable Linear Low Density Polyethylene Resin Product Description: LL 1002YB is a C4 Ziegler Natta LLDPE for Low Voltage power cable and Telecom jacketing. The grade contains a higher level of antioxidants and has excellent Environmental Stress..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
Entec Hypel® PELD50/.924 LDPE Available in North America Features: Food Contact Acceptable and Low DensityAgency Ratings: FDA 21 CFR 176.170, Table 2, Cond. B; Cond. C; Cond. D; Cond. E; Cond. F; Cond. G; Cond. H; and FDA 21 CF..
Tensile Strength, Yield	11.7 MPa	1700 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Dow DNDA-7144 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-7144 NT 7 is produced using UNIPOL™ PE process technology. It is intended for use in injection molding applications such as large industrial containers and trash cans. Information provide..
Tensile Strength, Yield	11.7 MPa	1700 psi	Molded property
Dow DOWLEX™ 2035 Linear Low Density Polyethylene, Cast Film Grade DOWLEX® 2035 Polyethylene resin is for cast film extrusion. It offers excellent tear strength, toughness and good processability. It complies with FDA regulation 21 CFR 177.1520(c) 3.2a when used u..
Tensile Strength, Yield	11.7 MPa	1700 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Dow GRSN-9820 NT 7 Linear Low Density Polyethylene Granular Solid DOW GRSN-9820 NT 7 is produced using UNIPOL™ PE process technology and is supplied in granular form. This resin is specifically designed as a carrier resin for color concentrates and other master ..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D-638
Axiall 8644 Moldings & Extrusions Flexible PVC General purpose extrusion compound. Forms a good bond with rigid PVC in co-extrusion applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	11.7 MPa	1700 psi	2 in/min (50 mm/min); ASTM D638
Bapolene® 1072 Polyethylene, Injection Grade A high flow general purpose injection molding resin with good gloss, toughness and stress crack resistance. This product meets FDA standards for food contact applications.Applications: Housewares, ..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D-638
Axiall 16640 Wire & Cable Flexible PVC Matte finish battery booster cable jacket with excellent low temperature properties.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D-638
Axiall 2134N Moldings & Extrusions Flexible PVC 105C plug molding compound. UL recognized component for 94 V-2 in all colors (0.75 mm min. thickness) and 94 V-0 in black and white (1.5 mm min. thickness). UL QMFZ2 recognized component.Informati..
Tensile Strength, Yield	11.7 MPa	1700 psi	100%; ASTM D412
Teknor Apex APEX® 3311-85 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses-Automotive Applications, Food Service Applications, General Purpose, Medical Applications, Profiles, To..
Tensile Strength, Yield	11.7 MPa	1700 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR Atomite Whiting Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	>= 11.7 MPa	>= 1700 psi
Trelleborg Offshore Vikotherm™ 73165 Insulative Elastomer Vikotherm™ is a rubber elastomer chemically modified to provide very high insulating characteristics while maintaining its inherent rubber properties in respect of seawater resistance, pressure res..