Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 5.50 MPa | 798 psi | 200%, post cured- 4 hours at 166°C; ASTM D412 |
Multibase SILASTIC® 7-6860 Dow-Corning Biomedical Grade Liquid Silicone Rubber Information provided by Multibase |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | ASTM D412 |
Polymax® Maxelast® P3650 TPE, PP Overmold or Standalone use Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesAuto PartsTool Hand GripsSporting GoodsWire & Cable ElectronicsMedical DevicesPlasti.. |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | ASTM D412 |
Precision Polymer Engineering F70R Fluorosilicone Rubber Red Fluorosilicone, 65-75 °IRHD. Fluorosilicone rubber having methyl, vinyl and fluorine substituent groups on the polymer chain. To meet Aerospace Specification DTD5583A Grade 70.Applications: S.. |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | ASTM D412 |
Precision Polymer Engineering S70N Silicone Rubber Silicone Rubber, 66-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. To meet UK Ministry of Defence Aircraft Materials Specification DTD5582A Grade .. |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | ASTM D412 |
Precision Polymer Engineering S80N Silicone Rubber Silicone Rubber, 76-85 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. To meet UK Ministry of Defence Aircraft Materials Specification DTD5582A Grade .. |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | M100 |
3M Dyneon™ Fluorel™ FE-5610Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series O-ring grades are the c.. |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | M100 |
3M Dyneon™ Fluorel™ FT-2481 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 68.6%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, 4% Ca(OH)2, 1.4% Dihydroxy Crosslinker, 0.4% Phosp.. |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | |
Kraton® D1102 + LDPE blend (50/50) Blending KRATON D and G polymers with PE significantly improves the toughness at both room and low temperatures. KRATON polymers are block segments of styrene and rubber monomers (A-B, A-B-A, or [A.. |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | Elastic; ASTM D412 |
Multibase Multi-Flex® A 4001 LC Black TPE Thermoplastic Elastomer Features: Heat Resistance, HighOzone ResistantCompression Set, Low Forms: PelletsProcessing Method:Injection Molding Information provided by Multibase |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers Softflex® 2701-1502R Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers Softflex® SF 5060 Overmold for Nylon Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | chs 20 in/min; ASTM D638 |
Diamond Polymers Softflex® SF 8900 Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | Film Property, 50 µm thickness; ASTM D882 |
Arkema Group OREVAC® 9314 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | cured 72 hrs @ RT |
ACC QM 264 QSI Quantum Silicones 60 Durometer Addition Cure Moldmaking Material QM 264 is a two component, room temperature addition cure silicone material. The cured rubber has excellent mechanical properties, good shelf-life stability, excellent physical properties and resin .. |
|||
Tensile Strength, Yield | 5.50 MPa | 798 psi | 50 mm/min |
Arkema Group Evatane® 1005 VN 4 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for flexible films with high transparency and very high mechanical properties. Examples: high strength stretch film, greenhous.. |