Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 29.5 MPa | 4280 psi | Crosshead speed - 2"min.; ASTM D638 |
LyondellBasell Alathon® M5562 High Density Polyethylene ApplicationsALATHON M 5562 is a copolymer with medium molecular weight distribution. This resin provides moderate stiffness, toughness and stress crack resistance. Typical applications include noz.. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D638 |
Flint Hills 11R12A Specialty Homopolymer Polypropylene Features: Good drop impact, radiation resistant. Product does not contain animal derived components and is phthalate-free.Applications: Injection MoldingInformation provided by Flint Hills Resour.. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | 50 mm/min; ASTM D638 |
LG Chemical 65IH HIPS High impact, Extrusion, Balanced mechanical properties, Good surface appearance with high gloss, Conforming to FDA CFR 177.1640, Excellent processability, Applications include refrigerator food tray.. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D638 |
IRPC Polimaxx Polene 3340H Polypropylene Random Copolymer CHARACTERISTICS: HIGH CLARITY, HIGH IMPACT, GOOD EXTRUDABILITY APPLICATIONS: BLOW MOLDING, SHEET EXTRUSION FOR COSMETIC BOTTLES, SHEET FOR THERMOFORMING, CLOSURES, FILES |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D638 |
IRPC Polimaxx Polene G2855 High Density Polyethylene CHARACTERISTICS:GOOD IMPACT STRENGTH, MEDUIM STIFFNESSGOOD PROCESSABILITYAPPLICATIONS:BLOW MOLDINGFOR CONTAINERS FROM A FEW ml TO ABOUT 20 LITRES, LUBRICANT BOTTLES,COSMETIC BOTTLES, CHEMICAL CONTAI.. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D638 |
IRPC Polimaxx Polene R1760 High Density Polyethylene CHARACTERISTICS: HIGH IMPACT STRENGTH, EXCELLENT SURFACE APPEARANCE, GOOD RIGIDITY CONTAIN UV STABILIZER ADDITIVEAPPLICATIONS: INJECTION MOLDING FOR CRATES, TRAYS, CASES, INDUSTRIAL PARTS, BINS, LAR.. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D638 |
JPJ Technologies PP C120 PP Copolymer Injection Molding Information provided by JPJ Technologies |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | At 50 mm/min; ISO 527-2 |
Borealis Bormed™ HF840MO Polypropylene Homopolymer for Medical Applications Bormed HF840MO is a polypropylene homopolymer intended for injection molding and is modified with an internal lubricant for products requiring a low surface friction (e.g. two-part syringes).Bormed .. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 809 is a 40% talc-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 809 is a 40% talc-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D638 |
Tipco Tipcolene® FPC 20 - 20% Calcium Carbonate Reinforced Polypropylene Homopolymer 20% Calcium Carbonate Filled PP HomopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 809 is a 40% talc-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 809 is a 40% talc-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 809 is a 40% talc-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 809 is a 40% talc-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D412 |
ACC SMP™ EP 1009 EPI Engineered Polymers Silicone Modified Polymer EP 1009, “Powered by Reactamine®Technology”, is a two component 100% solid Silicone Modified Polyurea with superior performance in industrial applications. EP 1009 displays extremely fast cure ti.. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D412 |
ACC ReactAmine® EP 350 EPI Engineered Polymers Polyurea ReactAmine® EP-350 is a two component 100% solid Polyurea with superior performance in industrial applications. EP-350 displays extremely fast cure times with excellent adhesions to different subst.. |
|||
Tensile Strength, Yield | 29.5 MPa | 4280 psi | At 50 mm/min; ISO 527-2 |
Borealis Bormed™ HD810MO Polypropylene Copolymer for Medical Applications Bormed HD810MO is a specially modified polypropylene homopolymer intended for use in medical and medical related applications, which have to be sterilized by radiation. Products molded in HD810MO a.. |