Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 21.0 MPa | 3050 psi | 150x10x4 mm specimen, 50 mm/min; ISO 527-1/527-2 |
Solvay Engineered Polymers SEQUEL® 1733HI Engineered Polyolefin
(discontinued **) Description: SEQUEL® 1733HI engineered polyolefin is designed for large, painted automotive exterior applications that require dimensional stability over a broad temperature range. This material e.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
Chevron Phillips HiD® 9638 HDPE Sheeting and Blown Film Resin
(discontinued **) Resin Type: Sheeting Resin for the Geomembrane Market; ASTM D 4976 Classification: PE 225, A 56507Applications:Cast Geomembrane Applications, Notion and Millinery Bags, Heavy Duty Shipping Sacks, In.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
Chevron Phillips HiD® 9642 HDPE Sheeting Resin
(discontinued **) Resin Type: Sheeting Resin for the Geomembrane Market; ASTM D 4976 Classification: PE 225, A 56507Applications:Blown Geomembrane Applications, Sanitary Landfill Liners, Waste Water Reservoir Contain.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
Ineos Styrenics 495F High-Impact Polystyrene Resin (Global) Description: High-impact, high-flow grade for a wide variety of applications, including appliance components, consumer electronics housings, magnetic and optical media, building and construction, pa.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ISO Method R527 |
LyondellBasell Astryn BR33GC Polypropylene Copolymer, Mineral Filled Key Features: conventional melt flow, high modulus, UV-stabilized, mineral-filled polypropylene copolymer, high rigidity, high impact strength, good dimensional stability, low foggingApplications: k.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON MD000IS PP LNP STAT-KON* MD000IS is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
A. Schulman PP 1329H-01 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1329H-01 is a natural high flow, medium impact polypropylene that is suitable for molding thin parts with long mold flow distances. It permits reduction of injection tem.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
A. Schulman PP 1467-01 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1467-01ApplicationPP 1467-01 meet FDA Regulation 21 CFR 177.1520, for all food contact applications.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | At 50 mm/min; ASTM D683 IV |
Borealis Borecene™ RM8402 Linear Polyethylene for Rotational Molding Borecene RM8402 is a third generation linear medium density natural polyethylene for rotational molding. The narrow molecular weight distribution imparted through metallocene catalyst technology pro.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
A. Schulman PP 1467-01 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1467-01ApplicationPP 1467-01 meet FDA Regulation 21 CFR 177.1520, for all food contact applications.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | 2 in/min; ASTM D638 |
A. Schulman PP 1500X-01 Polypropylene High Impact Copolymer Polypropylene DescriptionPolypropylene PP 1500X-01 is a specially formulated high impact copolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ISO 527 |
A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer DescriptionFormion® FI 1051E is a non-reinforced, transparent, extrusion grade Sodium Ionomer. It has been formulated for high durability, cut and puncture resistance, and low temperature ductilit.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 3711 High Impact Polypropylene DescriptionPolyfort® FPP 3711 is a 26% calcium carbonate filled high impact polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | 2 in/min; ASTM D638 |
A. Schulman PP 1500X-01 Polypropylene High Impact Copolymer Polypropylene DescriptionPolypropylene PP 1500X-01 is a specially formulated high impact copolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | >= 21.0 MPa | >= 3050 psi | Requirement |
Westlake Plastics Lennite® GUR1020 (Type I) Ultra-high Molecular Weight Polyethylene For Medical Applications Medical grade Lennite UHMWPE is produced from premium resins in accordance with ASTM specification F648 and International Standard ISO 5834-1 for surgical implants. Westlake Plastics' proprietary m.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ISO 527 |
A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer DescriptionFormion® FI 1051E is a non-reinforced, transparent, extrusion grade Sodium Ionomer. It has been formulated for high durability, cut and puncture resistance, and low temperature ductilit.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | 50 mm/min, type I bar; ASTM D638 |
A. Schulman POLYFORT™ FTP 3130H-01/FTP 3130HU-Colors DescriptionPolyfort® FTP 3130H-01 (non-UV stabilized) and FTP 3130HU-Colors (UV-stabilized) are high flow injection molding polyolefin alloys which exhibit an exceptional stiffness-impact balance a.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
A. Schulman PP 1579 Polypropylene Impact Grade Polypropylene DescriptionPolypropylene PP 1579 is an impact grade of polypropylene for use in parts which require good impact and good appearance in light weight injection molded parts. Information provided by A.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | 2 in/min, Type IV bar; ASTM D-638 |
Chevron Phillips Marlex® HMN TR-942/942G Polyethylene; HDPE High density polyethylene. These hexene copolymers are tailored for rotational molding applications that require: Wide process windows and fair flowLong-term UV stabilizationExcellent impact stren.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3040 psi | 2.0 in/min; ASTM D638 |
ExxonMobil PP7505KNE2 Polypropylene Homopolymer Product Description: A medium to high impact copolymer designed for injection molded large consumer and industrial parts requiring high melt flow rate.Availability: North America Features:Balanced .. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
Clariant Remafin PP1100NAT Polypropylene Impact Modified Copolymer Data provided by Clariant Masterbatches |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ISO R 527 |
Arkema Group OREVAC® 18750 Maleic Anhydride Modified Polypropylene DescriptionOREVAC 18750 is a coextrusion coating adhesive based on a maleic anhydride modified polypropylene resin. It combines the processability of an extrusion coating resin with the thermal resi.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | 50 mm/min |
Arkema Group Pebax® 7033 SN 01 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE (PEBA) hardness 70 shore D Non plasticized flexible Polyamide Outstanding mechanical properties at low temperature (-40°C) Applications: Sport (Football shoe sole, ski top lay.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM-D638 |
Braskem ML4400N LLDPE Rotomolding Polyethylene The resin ML4400N is a linear low-density polyethylene, 1-butene based, with high stiffness and an adequate balance of processability and environmental stress cracking resistance. It contains long t.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | |
BASF Novolen® 2660 M Polypropylene UV stabilized grade for injection molded parts.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D-638 |
Axiall 35551 Wire & Cable Flexible PVC TW, THW insulation compound suitable for 105°C AWM applications. Oil II rated and VW-1. CSA approved for TR64, TR32, TEW, and AW.Information provided by Georgia GulfGeorgia Gulf became Axiall Cor.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ISO R 527 |
Addiplast Addilene PMD 50284 Polypropylene Copolymer Mineral reinforced, improved rigidityInformation provided by Addiplast. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | |
TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR Dixie Clay Filler MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | Z direction; ASTM D638 |
ALM D80-ST Nylon 11 SLS Prototyping Polymer Unfilled, color stabilized nylon 11 material that is also stabilized to prevent premature thermal degradation. Parts produced from PA D80-ST exhibit superior mechanical properties. Relatively inexp.. |
|||
Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
Ineos Nova 5504 High Impact Polystyrene
(discontinued **) Good overall balance of properties, USP Class VIApplications: Audio cassettes and cartridges, Housewares, Toys, Structural foam, Machine housings, Window framesProperties were determined on injectio.. |