Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 206 MPa @Thickness 3.20 mm |
29900 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
LG Chemical LUMID HM2604AW PA6+GF60% Feature: Injection Molding, PA6+GF60%Application: Bath liftInformation provided by LG Chemical |
|||
Tensile Strength, Yield | 206 MPa | 29900 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF35 L UV 35% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 35% Filler by WeightAdditive: Lubricant, UV Stabilizer and Heat StabilizerFeatures: Lubricated, Good UV Resi.. |
|||
Tensile Strength, Yield | 206 MPa | 29900 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF40 L 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: LubricantFeatures: LubricatedProcessing Method: Injection MoldingInformation p.. |
|||
Tensile Strength, Yield | 206 MPa | 29900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PF00C PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PF00C is a compound based on PA6 resin containing Glass Fiber. |
|||
Tensile Strength, Yield | 206 MPa | 29900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PF00CS PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PF00CS is a compound based on PA6 resin containing Glass Fiber. |
|||
Tensile Strength, Yield | 206 MPa @Strain 0.200 % |
29900 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum Grade 1 Titanium (UNS R50250) Uses: CPI equipment, industrial components, plate frame heat exchangers.Mechanical property data below is typical of annealed samples at room temperature.Information provided by Allegheny Ludlum. |
|||
Tensile Strength, Yield | 206 MPa @Strain 0.200 % |
29900 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum Grade 17 Titanium (UNS R52252) Uses: CPI equipment, industrial components, plate frame heat exchangers.Mechanical property data below is typical of annealed samples at room temperature.Information provided by Allegheny Ludlum. |
|||
Tensile Strength, Yield | 206 MPa @Strain 0.200 % |
29900 psi @Strain 0.200 % |
Typical; Annealed |
ATI Allegheny Ludlum AL 4750™ Electrical Alloy, UNS K94800 or UNS K95000 The alloy produces good magnetic properties, wide latitude to control hysteresis loop shape via recrystallization modes. Applications for this grade range from electromechanical relay cores, to ver.. |
|||
Tensile Strength, Yield | 206 MPa | 29900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP VERTON RX00327 PA 66 LNP* VERTON* RX00327 is a compound based on Nylon 66 resin containing proprietary fillers. Added feature of this material is: Structural. |