Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 335 MPa @Strain 0.200 %, Temperature 150 °C |
48600 psi @Strain 0.200 %, Temperature 302 °F |
EN min.; EN 10002-5 |
Outokumpu 2205 Duplex Stainless Steel Duplex stainless combining high mechanical strength with good corrosion resistance.Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical t.. |
|||
Tensile Strength, Yield | >= 335 MPa @Temperature 20.0 °C |
>= 48600 psi @Temperature 68.0 °F |
Condition T4 (Quenching in water at RT) |
PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition T4 Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
Tensile Strength, Yield | 335 MPa @Thickness 12.7 mm, Temperature 260 °C |
48600 psi @Thickness 0.500 in, Temperature 500 °F |
0.2% Offset |
Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
Tensile Strength, Yield | 335 MPa @Thickness 12.7 mm, Temperature 20.0 °C |
48600 psi @Thickness 0.500 in, Temperature 68.0 °F |
0.2% offset |
Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
Tensile Strength, Yield | 335 MPa @Strain 0.200 % |
48600 psi @Strain 0.200 % |
Typical |
Aleris Weldural Aluminum Alloy, 200 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |